The invention discloses a low temperature impact polyester composition and a preparation method thereof. The low temperature resistant polyester composition is made up of the following ingredients: PBT resin, POK, TPEE elastomer, MBS toughening agent, compatibilizer, transesterification inhibitor, antioxidant and lubricant. Meanwhile, the preparation method of the low temperature impact polyester compound is also disclosed. The polyester composition of the invention has higher heat resistance and punching resistance than ordinary PBT polyester, especially at low temperature. The polyester composition has the characteristics of solvent corrosion resistance, ultraviolet resistance and so on. The polyester composition of the invention has simple preparation process, simple operation and low cost, and can be applied to the field of lamp bracket, automobile interior and exterior decorations, medical parts, etc.
【技术实现步骤摘要】
一种耐低温冲击聚酯组合物及其制备方法
本专利技术涉及一种耐低温冲击聚酯组合物及其制备方法。
技术介绍
PBT(聚对苯二甲酸丁二醇酯)树脂是一种结晶性的热塑性聚酯，具有优异的耐化学腐蚀，高流动性，易染色性，近年来获得了广泛的应用，主要用于汽车零部件，机械设备，电子电器等方面的应用。但未经改性的PBT相比其他工程塑料而言仍有很多缺点，比如热变形温度约为45～60℃，缺口冲击强度只有3～6kJ/m2，这极大低限制了PBT的使用，因此必须对其进行改性，才能满足工业上更为严苛的要求。CN103772934A公开了一种高抗冲、高耐热PC/PBT合金材料及其制备工艺，主要采用高抗冲和高耐热的PC与PBT共混来达到目的。但是PC的熔体强度大，与PBT共混的熔体相容性较差，需要添加较大量的相容剂。另外，PC的熔点高，导致加工温度大，容易发生分解和酯交换反应。CN105255149A公开了一种低温增韧增强PC/PBT合金材料及其制备方法，通过添加低温增韧剂来提高合金的低温冲击性能。但是并没有公布该合金材料在常温下的冲击性能及耐热性能。另外，PC的添加量达50％左右，造成合金的制造成本...
【技术保护点】
一种耐低温冲击聚酯组合物，其特征在于：由以下质量份的原料组成：
【技术特征摘要】
1.一种耐低温冲击聚酯组合物，其特征在于：由以下质量份的原料组成：2.根据权利要求1所述的一种耐低温冲击聚酯组合物，其特征在于：PBT树脂的缺口冲击强度为3kJ/m2～6kJ/m2；PBT树脂在1.82MPa下的热变形温度为45℃～60℃。3.根据权利要求1所述的一种耐低温冲击聚酯组合物，其特征在于：POK在240℃，2.16kg下的熔融指数为40g/10min～120g/10min；POK在1.82MPa下的热变形温度为210℃～220℃。4.根据权利要求1所述的一种耐低温冲击聚酯组合物，其特征在于：TPEE弹性体的硬段为结晶PBT，软段为非晶的脂肪族聚酯或聚醚。5.根据权利要求1所述的一种耐低温冲击聚酯组合物，其特征在于：相容剂为苯乙烯-丙烯腈-甲基丙烯酸缩水甘油酯共聚物。6.根据权利...
【专利技术属性】
技术研发人员：李函坚，杨海民，张宗豪，
申请(专利权)人：广东聚石化学股份有限公司，
类型：发明
国别省市：广东,44