The invention discloses a kind of cable sheath material, which is made up of the weight portion of the following raw materials: 50 carboxyl nitrile rubber rubber 80, 10 silicone 30, 1 antioxidant 5, 2 flame retardant 3, 3 plasticizer 6 copies, 6 8 copies of furnace carbon black, Zinc Oxide 1 6 copies, raw rubber matrix, calcium silicate of active silica , graphene 1, 3, 2 acidified starch 6, silane 1, 2, basalt fiber 4, 6, compound stabilizer 1 3, modified lime, 3, 3. The sheath material used in the invention has the characteristics of good flame retardancy, high tensile strength, high elongation and friendly environment, and is very suitable for all kinds of cable materials to improve the stability and safety of the cable.
【技术实现步骤摘要】
一种电缆用护套材料
本专利技术涉及一种电缆用护套材料。
技术介绍
近几十年来，橡胶材料及其制品得到蓬勃发展，它正迅速代替钢材、金属、水泥及木材、棉等天然聚合物被广泛应用于工业、农业、军事等国民经济的各个部门。作为电缆外层护套材料的橡胶，其大多合成材料属于易燃、可燃材料，而阻燃材料则往往含有很高的卤素，在燃烧过程中可产生大量的有毒气体，造成对环境的危害，对人们的生命安全形成巨大威胁，因此，如何提高合成材料的阻燃性能并降低其燃烧时产生的毒性物质，已成为一个急需解决的问题。
技术实现思路
本专利技术的目的就在于为了解决上述问题而提供一种阻燃性好、拉伸强度高、伸长率高、环境友好的电缆用护套材料。为了实现上述目的，本专利技术是通过以下技术方案实现的：一种电缆用护套材料，其按照以下原料的重量份数组成：羧基丁腈橡胶50-80份、硅树脂10-30份、防老剂1-5份、阻燃剂2-3份、增塑剂3-6份、炉法炭黑6-8份、氧化锌1-6份、生胶基体10-15份、活性硅酸钙15-30份、石墨烯1-3份、酸化淀粉2-6份、硅氮烷1-2份、玄武石纤维4-6份、复合稳定剂1-3份、改性生石灰3-5份。...
【技术保护点】
一种电缆用护套材料，其特征在于：按照以下原料的重量份数组成：羧基丁腈橡胶50‑80份、硅树脂10‑30份、防老剂1‑5份、阻燃剂2‑3份、增塑剂3‑6份、炉法炭黑6‑8份、氧化锌1‑6份、生胶基体10‑15份、活性硅酸钙15‑30份、石墨烯1‑3份、酸化淀粉2‑6份、硅氮烷1‑2份、玄武石纤维4‑6份、复合稳定剂1‑3份、改性生石灰3‑5份。
【技术特征摘要】
1.一种电缆用护套材料，其特征在于：按照以下原料的重量份数组成：羧基丁腈橡胶50-80份、硅树脂10-30份、防老剂1-5份、阻燃剂2-3份、增塑剂3-6份、炉法炭黑6-8份、氧化锌1-6份、生胶基体10-15份、活性硅酸钙15-30份、石墨烯1-3份、酸化淀粉2-6份、硅氮烷1-2份、玄武石纤维4-6份、复合稳定剂1-3份、改性生石灰3-5份。2.根据权利要求1所述的一种电缆用护套材料，其特征在于：按照以下原料的重量份数组成：羧基丁腈橡胶50-75份、硅树脂10-25份、防老剂1-4份、阻燃剂2-3份...