一种玻璃钢涂覆前针孔修复的方法技术

本发明专利技术公开了一种玻璃钢涂覆前针孔修复的方法，解决了现有技术中在玻璃钢底材上刮涂一般腻子填充针孔导致的漆层结合力差易起皮的问题。本发明专利技术包括在玻璃钢喷涂底漆之前，采用小分子量官能团的清漆喷涂在玻璃钢上，烘干即可；所述清漆的粘度为14～20S。喷涂在玻璃钢上的清漆的厚度不小于20um。本发明专利技术具有提高成品质量，使成品更加平整光滑等优点。

A method of repairing the pinhole before the coating of glass fiber reinforced plastics

The invention discloses a method for repairing the pinhole before the coating of glass steel, and solves the problem that the coating of the general putty is filled with the needle hole of the general putty on the glass steel bottom material, and the problem of the poor bonding force of the lacquer layer is poor and the skin is easy to be peeling. The invention can be dried with a small molecular weight functional group of varnish on glass steel before spraying the primer to the glass steel. The viscosity of the varnish is 14 to 20S. The thickness of varnish sprayed on FRP is not less than 20um. The invention has the advantages of improving the quality of finished products and making the finished products more smooth and smooth.

【技术实现步骤摘要】
一种玻璃钢涂覆前针孔修复的方法
本专利技术涉及一种修复方法，具体涉及一种玻璃钢涂覆前针孔修复的方法。
技术介绍
玻璃钢是一种质量轻、强度高、绝缘的材料，它以树脂为主料，以玻璃纤维为增强材料。玻璃钢耐腐蚀，对水和一般浓度的酸、碱、盐都有较好的抵抗能力，有较好的成型性。被广泛地应用于各个行业。玻璃钢产品底材有针孔缺陷，在涂覆过程中，表面针孔会造成漆面凹坑，采用一般腻子填充针孔，漆层结合力差易起皮。漆面防护效果差，外观标准达不到要求。
技术实现思路
本专利技术所要解决的技术问题是：现有技术中在玻璃钢底材上刮涂一般腻子填充针孔导致的漆层结合力差易起皮的问题，本专利技术提供了解决上述问题的一种玻璃钢涂覆前针孔修复的方法。本专利技术通过下述技术方案实现：一种玻璃钢涂覆前针孔修复的方法，包括：在玻璃钢喷涂底漆之前，采用小分子官能团的清漆喷涂在玻璃钢上，烘干即可。本专利技术中小分子官能团为分子所含的官能团相对原子质量较小，其相对原子质量一般小于5000g/mol，如S01-20清漆或环氧聚酰胺清漆，其就是小分子官能团的清漆。进一步，所述清漆的粘度为14～20S。喷涂在玻璃钢上的清漆的厚度不小于20um。本文档来自技高网...

【技术保护点】
一种玻璃钢涂覆前针孔修复的方法，其特征在于，包括：在玻璃钢喷涂底漆之前，采用小分子官能团的清漆喷涂在玻璃钢上，烘干即可。

【技术特征摘要】
1.一种玻璃钢涂覆前针孔修复的方法，其特征在于，包括：在玻璃钢喷涂底漆之前，采用小分子官能团的清漆喷涂在玻璃钢上，烘干即可。2.根据权利要求1所述的一种玻璃钢涂覆前针孔修复的方法，其特征在于，所述清漆的粘度为14～20S。3.根据权利要求1所述的一种玻璃钢涂覆前针孔修复的方法，其特征在于，喷涂在玻璃钢上的清漆的厚度不小于20um。4.根据权利要求3所述的一种玻璃钢涂覆前针孔修复的方法，其特征在于，喷涂在玻璃钢上的清漆的厚度为25～45um。5.根据权利要求1所述的一种玻璃钢涂覆前针孔修复的方法，其特征在于，所述喷涂的压力为0.3～0...

【专利技术属性】
技术研发人员：张威，褚勇卫，杨元志，郭果，杨钞，文浩，陶峰，
申请(专利权)人：四川九洲电器集团有限责任公司，
类型：发明
国别省市：四川,51