The invention discloses a sodium refining agent for aluminum alloy smelting. The refining agent is made up of the following raw materials: calcium fluoride 10, 16 copies of potassium fluoride, 10 potassium fluoride, 14 potassium fluoride, 8 potassium chloride 12, 8 lithium chloride 14, 8 magnesium chloride 14, titanium dioxide 6 10 copies, carbon powder fractions. The dehydrogenation effect of the refining agent in the refining process is remarkable, and the oxide inclusion in the melt can be removed fully, and the recovery of hot slag is more convenient and the recovery rate is higher. It is also because titanium will play a certain role in refining the alloy. It contains no sodium salt and has good refining effect.
【技术实现步骤摘要】
一种用于铝合金熔炼的无钠精炼剂
本专利技术涉及一种用于铝合金熔炼的无钠精炼剂，属于铝合金铸造
技术介绍
铝合金是工业中应用最广泛的一类有色金属结构材料，在航空、航天、汽车、机械制造、船舶及化学工业中已大量应用。铝合金在生产的过程中，溶液内的氢原子会自发形成氢气，氢气和夹杂物在铝合金溶液凝固的过程中形成气泡，使得铝合金构件产生缺陷。目前，我国公开的精炼剂中一般都含有氯化钠、氟铝酸钠、氟化钠、氟硅酸钠、硫酸钠等钠盐的一种或多种，这种钠盐的使用，会向铝镁、铝铜、铝锂系合金中引入钠，从而产生“钠脆”现象。
技术实现思路
本专利技术为解决上述问题，提供了一种用于铝合金熔炼的无钠精炼剂，该精炼剂由以下重量份的原料配制而成：氟化钙10-16份，氟硅酸钾10-14份，氟钛酸钾10-14份，氯化钾8-12份，氯化锂8-14份，氯化镁8-14份，二氧化钛6-10份，碳粉3-5份。进一步的，一种用于铝合金熔炼的无钠精炼剂，该精炼剂由以下重量份的原料配制而成：氟化钙10份，氟硅酸钾10份，氟钛酸钾10份，氯化钾8份，氯化锂8份，氯化镁8份，二氧化钛6份，碳粉3份。进一步的，一种用于铝合金熔炼的无钠精炼剂，该精炼剂由以下重量份的原料配制而成：氟化钙16份，氟硅酸钾14份，氟钛酸钾14份，氯化钾12份，氯化锂14份，氯化镁14份，二氧化钛10份，碳粉5份。进一步的，一种用于铝合金熔炼的无钠精炼剂，该精炼剂由以下重量份的原料配制而成：氟化钙13份，氟硅酸钾12份，氟钛酸钾12份，氯化钾10份，氯化锂11份，氯化镁11份，二氧化钛8份，碳粉4份。本专利技术的有益效果是：本专利技术的...
【技术保护点】
一种用于铝合金熔炼的无钠精炼剂，其特征在于，该精炼剂由以下重量份的原料配制而成：氟化钙10‑16份，氟硅酸钾10‑14份，氟钛酸钾10‑14份，氯化钾8‑12份，氯化锂8‑14份，氯化镁8‑14份，二氧化钛6‑10份，碳粉3‑5份。
【技术特征摘要】
1.一种用于铝合金熔炼的无钠精炼剂，其特征在于，该精炼剂由以下重量份的原料配制而成：氟化钙10-16份，氟硅酸钾10-14份，氟钛酸钾10-14份，氯化钾8-12份，氯化锂8-14份，氯化镁8-14份，二氧化钛6-10份，碳粉3-5份。2.根据权力要求1所述的一种用于铝合金熔炼的无钠精炼剂，其特征在于，该精炼剂由以下重量份的原料配制而成：氟化钙10份，氟硅酸钾10份，氟钛酸钾10份，氯化钾8份，氯化锂8份，氯化镁8份，二氧化钛6份，碳粉...
【专利技术属性】
技术研发人员：魏道金，
申请(专利权)人：徐州轩辕铝业有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。