The invention relates to a coating, in particular to a waterproof coating with self repairing ability. It is characterized by the following components: the composition and weight percentage of Portland cement 70, 80% stone powder, 4 calcium carbonate, 4 calcium carbonate 6%, 3 active masterbatch 5%, 3 antioxidant 5%, 1 silicates 3%, titanium dioxide 3 5%, dry powder sucrose The sand is 13 and 15%. The invention has super permeability, which permeate and crystallize inside concrete. It is not easy to be destroyed; with unique self repairing ability, it can repair cracks less than 0.4mm, prevent the damage of chemical corrosion to concrete structure and protect the steel bar. Non toxic, harmless and environment-friendly products, heat resistance, moisture resistance, oxidation resistance, carbonization, UV resistance and radiation resistance.
【技术实现步骤摘要】
一种具备自我修复能力的防水涂料
本专利技术涉及一种涂料，具体涉及一种水泥素浆、砂浆、混凝土防水、防渗漏的高性能具备自我修复能力的防水涂料。
技术介绍
混凝土是一种多孔物质，毛细孔和微裂纹是引起渗漏的根本原因。如果将毛细孔通道和微裂纹堵塞，就能够起到防水、抗渗的作用，而水泥基渗透结晶型具备自我修复能力的防水涂料是利用这一原理来达到防水目的的。这些具备自我修复能力的防水涂料具有生产工艺简单、施工方便、防水、抗渗的功能。但存在二次抗渗压力差，防水效果不稳定等问题。为解决这一问题专利技术了该涂料。
技术实现思路
本专利技术为了克服现有涂料的缺点，提供一种具备自我修复能力的防水涂料。本专利技术的技术方案是：一种具备自我修复能力的防水涂料，其特征在于由以下成分组成，其成分和重量百分比为：硅酸盐水泥70-80％，石粉2-3％，碳酸钙4-6％，活性母料3-5％，防老剂3-5％，硅酸盐1-3％，钛白粉3-5％，干粉状蔗糖0.3-0.5％，羟丙基甲基纤维素85-100目，石英砂13-15％。一种具备自我修复能力的防水涂料的制备方法，其特征在于：由以下步骤构成：将各成分按比例准确备用，使用...
【技术保护点】
一种具备自我修复能力的防水涂料。其特征在于：由以下成分组成，其成分和重量百分比为：硅酸盐水泥70‑80％，石粉2‑3％，碳酸钙4‑6％，活性母料3‑5％，防老剂3‑5％，硅酸盐1‑3％，钛白粉3‑5％，干粉状蔗糖0.3‑0.5％，羟丙基甲基纤维素85‑100目，石英砂13‑15％。
【技术特征摘要】
1.一种具备自我修复能力的防水涂料。其特征在于：由以下成分组成，其成分和重量百分比为：硅酸盐水泥70-80％，石粉2-3％，碳酸钙4-6％，活性母料3-5％，防老剂3-5％，硅酸盐1-3％，钛白粉3-5％，干粉状蔗糖0.3-0.5％，羟丙基甲基纤维素85-100目，石英砂13-15％。2.根据权利要求1所述的一种具备自我修复能力的防水涂料，其特征在于：这种具备自我修复能力的防水涂料的制备方法为：将各成分按比例准确备用，使用悬臂双...