The invention provides a processing method for the cover cloth of a military card canopy. It solves the problem that the structure of the existing canopy cloth is too simple and has no waterproof, corrosion resistant and climate resistant functions, single use, and no processing methods. The processing method of the military card cover cover includes the following steps: A, select the line density sold by the market, the 1000D*1000D polyester silk fabric as the base cloth; B, 115 PVC paste resins, 28 plasticizers, 6 stabilizers, 18 flame retardants, 8 adhesives, 4 titanium dioxide, 12 heat insulation powder and 21 pigment. A PVC coating is made in a blender; C, the base cloth layer in step a is put into the coating device, and the PVC coating in step B is poured into the mixing bucket of the coating device, and the PVC coating is evenly coated on the bottom of the base cloth layer to form a PVC coating; D, which will be dried for the base cloth layer that will be painted a good PVC coating. The invention has the advantages of high quality of the product.
【技术实现步骤摘要】
一种军用卡车篷盖布的加工方法
本专利技术涉及一种军用卡车篷盖布的加工方法。
技术介绍
篷盖布是在织物上覆盖一层高分子涂层剂或其它材料制成的复合材料。这种复合材料不仅具有织物原有的性能和功能,更增加了涂层的性能和功能。由于可供选择的基布和涂层材料品种很多,加上涂层工艺的变化,因而篷盖布的品种繁多,功能齐全,适用面很广。经检索,如中国专利文献公开了一种隔热耐老化PVC篷盖布【申请号:201410702441.6;公开号:CN105619976A】。这种隔热耐老化PVC篷盖布,其特征在于,由网格布双面涂敷PVC涂层组成,所述PVC涂层的原料配方按照重量份数包括以下组分:PVC糊树脂80份、氯化聚乙烯10~30份、邻苯二甲酸二辛酯40-85份、空心玻璃微珠10~20份、碳酸钙20-35份、稳定剂3-6份、抗氧化剂0-10份、粘合剂1-8份。该专利中公开的篷盖布虽然可以减少对光热的吸收,提高其耐老化性能,但是,该篷盖布的结构过于简单,没有防水、耐腐蚀和耐气候的功能,使用单一,且没有加工方法,因此,设计出一种军用卡车篷盖布的加工方法是很有必要的。
技术实现思路
本专利技术的第一个目的是针对现有的技术存在上述问题,提出了一种军用卡车篷盖布,该篷盖布具有实用性强的特点。本专利技术的第一个目的可通过下列技术方案来实现:一种军用卡车篷盖布,包括基布层,其特征在于,所述基布层上下侧均设置有PVC涂层,所述PVC涂层包括以下重量份的组分:PVC糊树脂110-120份、增塑剂25-30份、稳定剂3-8份、阻燃剂10-25份、粘合剂6-10份、钛白粉2-6份、隔热粉8-16份和颜料18- ...
【技术保护点】
一种军用卡车篷盖布的加工方法,其特征在于,该方法包括以下步骤:a、选取市场出售的线密度,1000D*1000D的涤纶丝机织布作为基布层,当然也可以选取市场上出售的其它类型的机织布作为基布层;b、称取PVC糊树脂115份、增塑剂28份、稳定剂6份、阻燃剂18份、粘合剂8份、钛白粉4份、隔热粉12份和颜料21份投入到搅拌机中,制得PVC涂液,搅拌时间为1.5h,搅拌机为市场上出售的现有的设备;c、将步骤a中的基布层放入到涂层装置中,将步骤b中的PVC涂液倒入到涂层装置的搅拌桶中,将PVC涂液均匀涂刷在基布层上下侧,形成PVC涂层;d、将涂刷好PVC涂层的基布层进行烘干,烘干温度为120℃,烘干时间为18h。
【技术特征摘要】
1.一种军用卡车篷盖布的加工方法,其特征在于,该方法包括以下步骤:a、选取市场出售的线密度,1000D*1000D的涤纶丝机织布作为基布层,当然也可以选取市场上出售的其它类型的机织布作为基布层;b、称取PVC糊树脂115份、增塑剂28份、稳定剂6份、阻燃剂18份、粘合剂8份、钛白粉4份、隔热粉12份和颜料21份投入到搅拌机中,制得PVC涂液,搅拌时间为1.5h,搅拌机为市场上出售的现有的设备;c、将步骤a中的基布层放入到涂层装置中,将步骤b中的PVC涂液倒入到涂层装置的搅拌桶中,将PVC涂液均匀涂刷在基布层上下侧,形成PVC涂层;d、将涂刷好PVC涂层的基布层进行烘干,烘干温度为120℃,烘干时间为18h。2.根据权利要求1所述的军用卡车篷盖布的加工方法,其特征在于,所述步骤c中的涂层装置包括机架,机架的材料为铸铁,所述机架上设置有涂层辊和放料槽,涂层辊位于放料槽正上方,涂层辊与一能带动其上下升降的升降结构相连,机架上设置有能对放料槽输送涂料的送料机构和能对涂层厚度进行调节的调节机构。3.根据权利要求2所述的军用卡车篷盖布的加工方法,其特征在于,所述送料机构包括上部开口的搅拌桶、调节板和安装架,搅拌桶通过支架固定在机架上,搅拌桶底部通过输送管和放料槽相连通,输送管中设置有输送泵,调节板滑动设置在搅拌桶内且将搅拌桶分为上搅拌部和下存料部,调节板上设置有能连通上搅拌部和下存料部的连接管,连接管中设置有电磁阀,机架上设置有使调节板向上移动的推动结构,安装架固定在机架上,安装架上设置有驱动气缸,驱动气缸的活塞杆竖直向下,驱动气缸的活塞杆端部和升降板相连,升降板上固定有步进电机,步进电机的输出轴竖直向下,步进电机的输出轴上固定有搅拌件。4.根据权利要求3所述的军用卡车篷盖布的加...
【专利技术属性】
技术研发人员:苏跃锋,张伟忠,凌建丰,沈金,陆慧斌,
申请(专利权)人:浙江汇锋薄膜科技有限公司,
类型:发明
国别省市:浙江,33