The invention discloses a high performance polypropylene composite plastic for water horse enclosure. Its raw material includes 95 main materials, 105 copies of main material, 1 transparent nucleating agent, 5 copies of peroxide two benzoyl 1, 6 parts of talcum powder compound 2, 1 barium sulfate, 1 glass fiber, 5, nano diatomite and compatibilizer The dispersant is 1, 2, 1, 2, 1, 1, 2, and 2. The talcum powder complex was prepared by the following process: polylactic acid, talcum powder, epoxy soybean oil, fourteen alkandiacid, and stannous chloride, and the talcum powder complex was heated and stirred. The present invention has high performance polypropylene composite plastic, excellent tensile strength and flexural modulus, good toughness, extremely strong anti ultraviolet performance, tensile strength and impact strength.
【技术实现步骤摘要】
一种水马围挡用高性能聚丙烯复合塑料
本专利技术涉及聚丙烯
，尤其涉及一种水马围挡用高性能聚丙烯复合塑料。
技术介绍
水马围挡是一种用于分割路面或形成阻挡的塑料制壳体障碍物，在其顶部设注水孔用于向内注水或细砂等增重物，两端分别设计有企口，可用于多个水马围挡之间构成首尾相接，从而形成较长的水马围挡墙。目前，水马围挡常用于道路交通设施，在高速路、城市道路及天桥街道路口作为道路分道、区域隔离、分流和导向，并起到维护交通秩序的作用。水马围挡因采用塑料制成，其在使用过程中，经常受到风吹、雨淋、日晒，其在长期使用过程中因逐渐老化导致表面变硬变脆，当其出现碰撞或倒地时，极易出现破损，降低了使用寿命。聚丙烯塑料质轻、无毒、无臭、防潮、机械强度、尺寸稳定性好、密封性好的优点，现今已广泛用于制造水马围挡。为了提高产品档次和质量，必须使聚丙烯的强度、韧性等性能得到加强。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种水马围挡用高性能聚丙烯复合塑料，拉伸强度和弯曲模量优异、韧性好、抗紫外线性能极强、抗拉强度和抗冲击强度较优异。本专利技术提出的一种水马围挡用高性能聚丙烯复合...
【技术保护点】
一种水马围挡用高性能聚丙烯复合塑料，其特征在于，其原料按重量份包括：主料95‑105份，透明成核剂1‑5份，过氧化二苯甲酰1‑2份，滑石粉复合物2‑6份，沉淀硫酸钡1‑5份，玻璃纤维2‑8份，纳米硅藻土4‑10份，相容剂1‑2份，分散剂1‑2份，抗氧化剂1‑2份，光稳定剂1‑2份，紫外线吸收剂1‑2份。
【技术特征摘要】
1.一种水马围挡用高性能聚丙烯复合塑料，其特征在于，其原料按重量份包括：主料95-105份，透明成核剂1-5份，过氧化二苯甲酰1-2份，滑石粉复合物2-6份，沉淀硫酸钡1-5份，玻璃纤维2-8份，纳米硅藻土4-10份，相容剂1-2份，分散剂1-2份，抗氧化剂1-2份，光稳定剂1-2份，紫外线吸收剂1-2份。2.根据权利要求1所述水马围挡用高性能聚丙烯复合塑料，其特征在于，滑石粉复合物采用如下工艺制备：将聚乳酸、滑石粉、环氧大豆油、十四烷二酸、氯化亚锡混合，升温搅拌得到滑石粉复合物。3.根据权利要求2所述水马围挡用高性能聚丙烯复合塑料，其特征在于，滑石粉复合物的制备工艺中，升温...
【专利技术属性】
技术研发人员：张先根，
申请(专利权)人：芜湖盈奇塑业有限公司，
类型：发明
国别省市：安徽,34