一种激光打印机墨粉制造技术

本发明专利技术涉及一种激光打印机墨粉，属于办公用品技术领域，其特征在于：其重量份组成为：聚乳酸树脂50～95份；着色剂3～50份；脱模剂1～10份；电荷控制剂0.3～5份；香味剂0.01～5份，二氧化硅5～10份，PH调节剂0.5～2份，过硫酸铵1～5份。本发明专利技术的有益效果是：树脂包覆颜料和蜡形成均匀的粉体，包覆均匀、呈近球形状且尺寸可控，边沿平滑，色彩均匀，持久不褪色，特别适合用作彩色激光打印墨粉。

A kind of laser printer toner

The invention relates to a laser printer toner, which belongs to the technical field of office supplies, which is characterized by: its weight component is 50~95 polylactic resin, 3~50 coloring agents, 1~10 demoulding agents, 0.3 to 5 charge control agents, 0.01 to 5 parts of the fragrance agent, 5~10 silicon dioxide, 0.5 to 2 PH modifiers and sulfuric acid. 1~5 copies of ammonium. The beneficial effect of the invention is that the resin coated pigment and wax form a uniform powder. The coating is uniform, the shape is near the ball and the size is controllable, the edge is smooth, the color is uniform, and the color is durable. It is especially suitable for color laser printing ink powder.

【技术实现步骤摘要】
一种激光打印机墨粉
本专利技术涉及办公用品
，特别是涉及一种激光打印机墨粉。
技术介绍
随着办公自动化的发展，复印机和打印机等耗材的使用越来越普遍，墨粉作为激光打印和静电复印的重要耗材之一，其生产制备也越来越受到广泛的重视。然而，目前所使用的墨粉褪色较快且色彩较差，不利于需长期存放和大量打印。
技术实现思路
为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种激光打印机墨粉。本专利技术的目的是通过以下技术方案来实现的：一种激光打印机墨粉，其特征在于：其重量份组成为：聚乳酸树脂50～95份；着色剂3～50份；脱模剂1～10份；电荷控制剂0.3～5份；香味剂0.01～5份，二氧化硅5～10份，PH调节剂0.5～2份，过硫酸铵1～5份。优选地，其重量份组成为：聚乳酸树脂50份；着色剂3份；脱模剂1份；电荷控制剂0.3份；香味剂0.01份，二氧化硅5份，PH调节剂0.5份，过硫酸铵1份。优选地，其重量份组成为：聚乳酸树脂95份；着色剂50份；脱模剂10份；电荷控制剂5份；香味剂5份，二氧化硅10份，PH调节剂2份，过硫酸铵5份。本专利技术的有益效果是：树脂包覆颜料和蜡形成均匀的粉体本文档来自技高网...

【技术保护点】
一种激光打印机墨粉，其特征在于：其重量份组成为：聚乳酸树脂50～95份；着色剂3～50份；脱模剂1～10份；电荷控制剂0.3～5份；香味剂0.01～5份，二氧化硅5～10份，PH调节剂0.5～2份，过硫酸铵1～5份。

【技术特征摘要】
1.一种激光打印机墨粉，其特征在于：其重量份组成为：聚乳酸树脂50～95份；着色剂3～50份；脱模剂1～10份；电荷控制剂0.3～5份；香味剂0.01～5份，二氧化硅5～10份，PH调节剂0.5～2份，过硫酸铵1～5份。2.根据权利要求1所述的一种激光打印机墨粉，其特征在于：其重量份组成为：聚乳酸树脂50...

【专利技术属性】
技术研发人员：丁传铭，
申请(专利权)人：成都丰睿视觉科技有限公司，
类型：发明
国别省市：四川,51