The invention discloses a polythene polypropylene polymer waterproof roll material for improving the aging properties of artificial climate, consisting of the following weight components: linear low density polyethylene resin 92, 95 parts, 1.5 titanium oxide 0.5, 0.1 dispersants 0.5, 5 activator 8; the activator is obtained by the following preparation method : (1) steam blasting treatment: the residue of Gardenia jasminoides extracted from water was put into steam blasting tank; (2) high shear homogenizing machine was treated by high shear homogenizer. The raw material obtained from step 1 was added to the equal weight of pure water, and the activator was obtained after drying.
【技术实现步骤摘要】
一种改善人工气候老化性能的聚乙烯丙纶高分子防水卷材
本专利技术属于建筑材料与石化
，具体涉及一种改善人工气候老化性能的聚乙烯丙纶高分子防水卷材。
技术介绍
聚乙烯丙纶防水卷材属于合成高分子防水卷材系列，它除了完全具有合成高分子卷材的全部优点外，其自身最突出的特点，在于其表面的网状结构，使其具有了自己独特的使用性能--水泥粘接。因高分子复合卷材可用水泥直接粘接，因此在施工过程中不受基层含水率的影响，只要无明水即可施工。这是其他防水卷材所不具备的。由于高分子复合卷材标面粗糙、摩擦系数大，在水利工程应用时，可直接埋设在砂土中，具有足够的稳定性。由于高分子复合卷材可与水泥材料在凝固过程中直接粘接，因此可直接设计在水泥材料的结构中。聚乙烯丙纶防水卷材具有构造特点：1、三层式结构，表面增强。2、芯层--主防水层采用了支比度较高(大分子侧链多)的线性低密度聚乙烯(LLDPE)，其延伸性、不透水性、柔软性、抗穿刺性、耐低温性能较好。3、表面为丙纶(涤纶)无纺布，通过与芯层的复合，解决了聚乙烯线胀系数大的不足。增加了产品表面的粗糙度，提高了产品的摩擦系数，并使复合卷材的粘接问...
【技术保护点】
一种改善人工气候老化性能的聚乙烯丙纶高分子防水卷材，其特征在于，由以下重量份的组分组成：线性低密度聚乙烯树脂92.0‑95.0份、氧化钛0.5‑1.5份、分散剂0.1‑0.5份、活性剂5.0‑8.0份；所述活化剂通过以下制备方法的得到：①蒸汽爆破处理：将水提取过的栀子残渣，放入蒸汽爆破罐处理；②高剪切均质机处理：将步骤①得到的物料，加入等重的纯净水，通过高剪切均质机处理，干燥后得到活化剂。
【技术特征摘要】
1.一种改善人工气候老化性能的聚乙烯丙纶高分子防水卷材，其特征在于，由以下重量份的组分组成：线性低密度聚乙烯树脂92.0-95.0份、氧化钛0.5-1.5份、分散剂0.1-0.5份、活性剂5.0-8.0份；所述活化剂通过以下制备方法的得到：①蒸汽爆破处理：将水提取过的栀子残渣，放入蒸汽爆破罐处理；②高剪切均质机处理：将步骤①得到的物料，加入等重的纯净水，通过高剪切均质机处理，干燥后得到活化剂。2.权利要求1所述的一种...