一种镀膜涂膜辊在线打磨方法技术

一种镀膜涂膜辊在线打磨方法，将一定目数的砂纸固定在专用擦板上，调整涂膜辊转速进行旋转，手持擦板在涂膜辊磨损区域进行打磨；打磨直至涂膜辊表面粗糙度达到正常区域的颜色后停止打磨，擦拭干净涂膜辊，本发明专利技术可以利用较短时间快速对涂膜辊磨损区域进行打磨，使其表面粗糙度恢复到原始状态，从而延长使用寿命，降低生产成本。

On line grinding method for coating film roll

An on-line grinding method for coating film roller is used to fix a certain number of sand paper on the special cleaning plate, adjust the speed of the coating roll and rotate, and the handheld eraser is worn in the wear area of the film roll, until the surface roughness of the coating roll reaches the normal area, and the coating roller is cleaned and the coating roll is cleaned. The invention can be used. In order to make use of short time to quickly wear the wear area of the coating roll, the surface roughness of the coating can be restored to the original state, thus prolonging the service life and reducing the production cost.

【技术实现步骤摘要】
一种镀膜涂膜辊在线打磨方法
本专利技术涉及镀膜涂膜辊
，特别涉及一种镀膜涂膜辊在线打磨方法。
技术介绍
光伏玻璃辊涂法镀膜是指将利用涂膜辊将镀膜液均匀涂布在光伏玻璃的表面。如图1所示，电雕辊和涂膜辊之间存有镀膜液，电雕辊将膜液均匀分度在涂膜辊上。由于光伏镀膜玻璃的边部磨削后粗糙度打，边部残留玻璃粉多，在滚涂镀膜生产中，涂膜辊在和玻璃边部接触区域会造成磨损老化，镀膜玻璃表面出现色差。通常做法是涂膜辊边部磨损造成色差时，必须更换涂膜辊，造成涂膜辊寿命低，生产成本增高。
技术实现思路
为了克服上述问题，本专利技术的目的在于提供一种镀膜涂膜辊在线打磨方法，解决镀膜玻璃边部色差问题，可以利用较短时间快速对涂膜辊磨损区域进行打磨，使其表面粗糙度恢复到原始状态，从而延长使用寿命，降低生产成本。为了实现上述目的，本专利技术采用的技术方案是：一种镀膜涂膜辊在线打磨方法，将一定目数的砂纸固定在专用擦板上，调整涂膜辊1转速进行旋转，手持擦板在涂膜辊1磨损区域进行打磨；打磨直至涂膜辊表面粗糙度达到正常区域的颜色后停止打磨，擦拭干净涂膜辊1。所述的砂纸为300-800目。所述的涂膜辊转速大于100转/min本文档来自技高网...

【技术保护点】
一种镀膜涂膜辊在线打磨方法，其特征在于，将一定目数的砂纸固定在专用擦板上，调整涂膜辊(1)转速进行旋转，手持擦板在涂膜辊(1)磨损区域进行打磨；打磨直至涂膜辊表面粗糙度达到正常区域的颜色后停止打磨，擦拭干净涂膜辊(1)。

【技术特征摘要】
1.一种镀膜涂膜辊在线打磨方法，其特征在于，将一定目数的砂纸固定在专用擦板上，调整涂膜辊(1)转速进行旋转，手持擦板在涂膜辊(1)磨损区域进行打磨；打磨直至涂膜辊表面粗糙度达到正常区域的颜色后停止打磨，擦拭干净涂膜辊(1)。2.根据权利要求1所述的一种镀膜涂膜辊在线打磨方法，其特征在于，所述的砂纸为300-600目。3.根据权利要求1所述的一种镀膜涂膜辊在线打磨方法，其特征在于，...

【专利技术属性】
技术研发人员：周昊，吴鹏，苏宇，
申请(专利权)人：彩虹集团新能源股份有限公司，
类型：发明
国别省市：陕西,61