The invention discloses a solar heat plate containing nickel carbide coating and a preparation method thereof, heat absorbing paint consists of the following portions of the quality of raw materials: 15 40 carbonized nickel chromium carbide, 5 15 copies, 15 copies, 5 alumina titanium silicide 5 15 copies, 5 copies, 3 iron powder rare earth 1 3, aluminum zirconium coupling agent 2 5 copies, 1 polymer dispersant 2, fluorine modified silicone resin 5 10 copies, 5 copies of 2 acetone and xylene 10 15. The invention has the advantages of simple preparation process, low cost, high stability of paint, and environmental protection, and has wide practical value and application prospect in the field of solar thermal utilization.
【技术实现步骤摘要】
一种含碳化镍的太阳能板吸热涂料及其制备方法
本专利技术属于新型涂料
,更具体地说是一种含碳化镍的太阳能板吸热涂料及其制备方法。
技术介绍
能源利用在人类社会发展中占有举足轻重的地位,但过度的开发资源和低效率的资源利用,使人类面临着严峻的考验。众所周知,太阳能是一种来源最丰富和可广泛获取的可再生能源,对解决能源危机和环境问题具有重大的作用,且太阳能以独具的储量无限性、存在的普遍性、开发利用的清洁性,使其成为了各国竞相研究的热点。太阳能吸收涂层主要分为光谱选择性吸收涂层和高吸收率吸收涂层,光谱选择性吸热涂层是一种具有对可见-近红外光高吸收,对红外光高反射的特种涂层,即它能有效地吸收太阳能,而受热后自身长波造成的热损失很小,广泛应用于太阳能光热转换,如太阳能热水器、太阳能发电等。太阳能吸热涂层担负着接收并吸收太阳能量的重要作用,影响着整个太阳能吸热系统的稳定性及效率的高低。目前市面上普遍采用的是在太阳能平板集热器的吸热板芯上喷涂黑色有机涂层,如黑色氟碳树脂、黑色环氧树脂、黑色聚氨酯树脂等,因为采用了普通的树脂材料作为粘合剂及以碳黑或者黑色颜料作为发色体,因此会造成:1、涂层不耐候,过早粉化和退色;2、由于采用的是普通碳黑或者黑色颜料作为发色体,无光谱选择性。因此它的涂层发射率很高,这样就造成了太阳能平板集热器的热效率低。
技术实现思路
针对现有技术的不足,本专利技术提供了一种含碳化镍的太阳能板吸热涂料及其制备方法,该涂料制备工艺简单,成本较低,涂料稳定性高,而且绿色环保,在太阳能热利用领域具有广阔的实用价值和应用前景。一种含碳化镍的太阳能板吸热涂料及其制备方法 ...
【技术保护点】
一种含碳化镍的太阳能板吸热涂料,其特征在于,所述吸热涂料由以下质量份数的原料制得:碳化镍15‑40份、碳化铬5‑15份、氧化铝5‑15份、硅化钛5‑15份、铁粉3‑5份、稀土1‑3份、铝‑锆偶联剂2‑5份、高分子分散剂1‑2份、氟改性硅树脂5‑10份、丙酮2‑5份和二甲苯10‑15份;所述高分子分散剂为阳离子聚丙烯酰胺分散剂。
【技术特征摘要】
1.一种含碳化镍的太阳能板吸热涂料,其特征在于,所述吸热涂料由以下质量份数的原料制得:碳化镍15-40份、碳化铬5-15份、氧化铝5-15份、硅化钛5-15份、铁粉3-5份、稀土1-3份、铝-锆偶联剂2-5份、高分子分散剂1-2份、氟改性硅树脂5-10份、丙酮2-5份和二甲苯10-15份;所述高分子分散剂为阳离子聚丙烯酰胺分散剂。2.根据权利...
【专利技术属性】
技术研发人员:丘秋燕,李正良,陈明贤,金秋生,郭家红,姚小龙,
申请(专利权)人:广西吉宽太阳能设备有限公司,
类型:发明
国别省市:广西,45