The invention discloses a biodegradable compatible binder for three dimensional printing, which is made from the following raw materials: phosphoric acid, polyvinyl alcohol, chondroitin sulfate, polyvinyl alcohol (PVA), citric acid, lecithin and deionized water. Phosphoric acid and polyvinyl alcohol glue have good biocompatibility. The chondroitin sulfate contained in the formula can further improve the biocompatibility of glue, and at the same time, in order to improve the printability of glue, lecithin is added into the formula. The biological binder is not only good for biological compatibility, but also suitable for printing of sprinkler, and can be used for three-dimensional biodegradable implants.
【技术实现步骤摘要】
一种用于三维打印可降解生物兼容粘结剂的配制方法
本专利技术提出一种可用于三维打印羟基磷灰石生物粘结剂的配制方法。主要涉及到生物活性材料研究、可喷墨打印生物胶水配制、3D打印技术、人工骨支架复合材料等几方面的研究。
技术介绍
三维打印是一种以数字模型文件为基础，使用粉末状可粘合材料，通过逐层打印的方式来构造产品的技术。目前,三维打印方法主要包括光固化成型工艺、叠层制造、选择性激光烧结、熔融沉积制造等。由于三维打印方法可快速生产具有复杂内部结构的定制化产品，能够很好地满足临床医用产品个性化及实时性的要求。然而，为了使用三维打印技术制造生物活性产品，可能造成生物材料理化变性或引入污染的方法是不可取的，因此，层叠粘结方法是目前最适用于生物活性产品制造的三维打印方法。层叠粘结制造中所选用粘结剂将直接影响产品的性能，为了更好地满足生物活性产品的三维打印制造，所选用的粘结剂应同时具有生物兼容性及良好的可打印性（可在现有三维打印设备上稳定使用，无堵塞、凝固等问题）。现有传统生物粘合剂主要用于替代外科手术中的缝合术，从而避免缝合术可能出现的副作用。这种粘合剂多使用外科胶黏剂、纤维蛋...
【技术保护点】
一种用于三维打印可降解生物兼容粘结剂，它是由以下重量份的原材料制成的：20%磷酸 100去离子水 10聚乙烯醇 0.4硫酸软骨素 0.9卵磷脂 10。
【技术特征摘要】
1.一种用于三维打印可降解生物兼容粘结剂，它是由以下重量份的原材料制成的：20%磷酸100去离子水10聚乙烯醇0.4硫酸软骨素0.9卵磷脂10。2.一种用于三维打印可降解生物兼容粘结剂，它是由以下重量份的原材料制成的：20%磷酸100去离子水30聚乙烯醇0.6硫酸软骨素0.7卵磷脂21。3.一种用于三维打印可降解生物兼容粘结剂，它是由以下重量份的原材料制成的...
【专利技术属性】
技术研发人员：侯祎波，杨明明，李欣培，毛海龙，
申请(专利权)人：西安博恩生物科技有限公司，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。