The invention discloses a reflective insulation coatings, it is composed of the following raw materials: silicone acrylic emulsion 180 200, 40, 30 sol dispersion of four hydroxymethyl phosphonium sulfate 1 2, 0.8 1, three ammonium myristic acid sodium soap 3, 4 to two tert butyl phenol 0.7 1, 6, 4 ethyl cellulose ester twelve coalescents 5 7, hollow glass bead 2.5 4, defoaming agent 0.8 1, the invention of the reflective insulation lacquer excellent weatherability, color fastness, durable, do not fade, especially suitable for painting on the external wall of a building, can most of the reflection of solar radiation, heat insulation, ensure the indoor temperature, because the stone mixture in the hollow glass bead, the lacquer has good sound insulation effect.
【技术实现步骤摘要】
一种反射隔热真石漆及其制备方法
本专利技术属于漆领域，具体涉及一种反射隔热真石漆及其制备方法。
技术介绍
现有技术中，较常见的真石漆适用于各类建筑物的室内外装修，具有防火、防水、耐酸碱、耐污染等特点，然而在大型建筑的外墙上，每天都需要接受强烈的太阳辐射，烈的太阳光照将热量从室外传递到室内，导致室内的温度升高，而太阳光所照射到的建筑物，最先与太阳光接触的就是建筑物外层的涂料层，因此，市面上急需具有反射隔热的真石漆。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种反射隔热真石漆及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种反射隔热真石漆，它是由下述重量份的原料组成的：硅丙乳液180-200、溶胶分散液30-40、四羟甲基硫酸磷1-2、三钼酸铵0.8-1、肉豆蔻酸钠皂3-4、叔丁基对二苯酚0.7-1、乙基纤维素4-6、醇酯十二成膜助剂5-7、空心玻璃微珠2.5-4、消泡剂0.8-1。所述的空心玻璃微珠的粒度为50-150μm。所述的消泡剂为聚二甲基硅氧烷。所述的溶胶分散液是由下述重量份的原料组成的：钛酸四丁酯40-50、烯丙基聚乙二醇6...
【技术保护点】
一种反射隔热真石漆，其特征在于，它是由下述重量份的原料组成的：硅丙乳液180‑200、溶胶分散液30‑40、四羟甲基硫酸磷1‑2、三钼酸铵0.8‑1、肉豆蔻酸钠皂3‑4、叔丁基对二苯酚0.7‑1、乙基纤维素4‑6、醇酯十二成膜助剂5‑7、空心玻璃微珠2.5‑4、消泡剂0.8‑1。
【技术特征摘要】
1.一种反射隔热真石漆，其特征在于，它是由下述重量份的原料组成的：硅丙乳液180-200、溶胶分散液30-40、四羟甲基硫酸磷1-2、三钼酸铵0.8-1、肉豆蔻酸钠皂3-4、叔丁基对二苯酚0.7-1、乙基纤维素4-6、醇酯十二成膜助剂5-7、空心玻璃微珠2.5-4、消泡剂0.8-1。2.根据权利要求1所述的一种反射隔热真石漆，其特征在于，所述的空心玻璃微珠的粒度为50-150μm。3.根据权利要求1所述的一种反射隔热真石漆，其特征在于，所述的消泡剂为聚二甲基硅氧烷。4.根据权利要求1所述的一种反射隔热真石漆，其特征在于，所述的溶胶分散液是由下述重量份的原料组成的：钛酸四丁酯40-50、烯丙基聚乙二醇6-7、三羟甲基丙烷0.6-1、硫化亚锡0.1-0.2、蓖麻酸钙0.8-2；所述的溶胶分散液的制备方法包括以下步骤：（1）取蓖麻酸钙，加入到其重量6-9倍的无水乙醇中，搅拌均匀，升高温度为75-80℃，加入硫化亚锡，保温搅拌1-2小时，得醇溶液；（2）取烯丙基聚乙二醇，加入...
【专利技术属性】
技术研发人员：朱宇红，
申请(专利权)人：佛山市嘉柏丽涂料有限公司，
类型：发明
国别省市：广东,44