The invention relates to the field of paint, in particular to a moisture proof and anticorrosion coating for packaging equipment. It is characterized in that: made from the following raw materials in parts by weight: polyurethane curing agent 40 60 copies, 30 copies, 20 polyurethane enamel ethylhexyl methacrylate 30 50 copies, 5 copies, 3 Zinc Oxide thickener 1 3, SEC butyl acetate 10 20 copies, 20 copies of 10 powder 10, titanium dioxide 30 copies, 80 copies, 60 xylene diisocyanate has 0.1 0.3 copies, 50 copies of 40 solution. The coatings, such as secondary butyl acetate, silica fume, titanium dioxide, xylene and diisocyanate, have excellent moisture resistance and outstanding anticorrosive properties.
【技术实现步骤摘要】
一种包装设备用防潮防腐涂料
本专利技术涉及涂料领域，具体涉及一种包装设备用防潮防腐涂料。
技术介绍
随着科技的发展，生活水平的提高，人们对健康安全的生活方式越来越关注。本专利技术主要用于易吸潮的材料，如水泥、砖块、纸张、包装盒、陶瓷等材料上，这些材料上涂上包装设备用防潮防腐涂料后，可以在低湿或高湿的环境下长时间放置而不会吸潮。
技术实现思路
本专利技术为了克服现有涂料的缺点，提供一种在高湿或低湿环境中防潮性能优异的包装设备用防潮防腐涂料。本专利技术的技术方案是：一种包装设备用防潮防腐涂料，由以下重量份数的原料制成：聚氨酯固化剂40-60份、聚氨酯磁漆20-30份、甲基丙烯酸异辛酯30-50份、氧化锌3-5份、增稠剂1-3份、硅粉10-20份、二氧化钛10-30份、二甲苯60-80份、已二异氰酸酯0.1-0.3份、水溶液40-50份。有益效果：本专利技术的包装设备用防潮防腐涂料组分合理，特别加入了聚氨酯固化剂和聚氨酯磁漆，两者在反应中产生的交联作用增强了其防水性和抗裂性，使本包装设备用防潮防腐涂料防潮性能优异，且聚氨酯磁漆的使用能增加本涂料的光洁度。具体实施方式以下结合实施例对本专利技术的原理和特征进行描述，所举实例只用于解释本专利技术，并非用于限定本专利技术的范围。实施例1一种包装设备用防潮防腐涂料，由以下重量份数的原料制成：聚氨酯固化剂40份、聚氨酯磁漆20份、甲基丙烯酸异辛酯30份、氧化锌3份、增稠剂1份、硅粉10份、二氧化钛10份、二甲苯60份、已二异氰酸酯0.1份、水溶液40份。实施例2一种包装设备用防潮防腐涂料，由以下重量份数的原料制成：聚氨酯固化剂...
【技术保护点】
一种包装设备用防潮防腐涂料，由以下重量份数的原料制成：聚氨酯固化剂40‑60份、聚氨酯磁漆20‑30份、甲基丙烯酸异辛酯30‑50份、氧化锌3‑5份、增稠剂1‑3份、仲丁基乙酸酯10‑20份、硅粉10‑20份、二氧化钛10‑30份、二甲苯60‑80份、已二异氰酸酯0.1‑0.3份、水溶液40‑50份。
【技术特征摘要】
1.一种包装设备用防潮防腐涂料，由以下重量份数的原料制成：聚氨酯固化剂40-60份、聚氨酯磁漆20-30份、甲基丙烯酸异辛酯30-50份、氧化锌3-5份、增稠剂1-3份、仲丁基乙酸酯10-20份、硅粉10-20份、二氧化钛10-30份、二甲苯60-80份、已二异氰酸酯0.1-0.3份、水溶液40-50份。2.根据权利要求1所述的包装设备用防潮防腐涂料，其特征在于其组成物的重量份为：聚氨酯固化剂40份、聚氨酯磁漆20份、甲基丙烯酸异辛酯30份、氧化锌3份、增稠剂1份、仲丁基乙酸酯10、硅粉10份、二氧化钛10份、二甲苯60份、已二异氰酸酯0...
【专利技术属性】
技术研发人员：吕世宁，
申请(专利权)人：山东蓝盟防腐科技股份有限公司，
类型：发明
国别省市：山东,37