The invention provides a EPE sheet preparation method and products, the method comprises the following steps: 1) preparing raw materials: polyethylene particles in 100 weight portions, nucleating agent 3.2 to 4.6 parts by weight, preferably 3.8 to 4.1 parts by weight; anti shrinking agent 0.7 to 1.5 parts by weight, preferably 0.9 to 1.2 parts by weight of foaming agent; 5.4 to 8.3 parts by weight, preferably 6.3 to 7.5 parts by weight; the raw materials are mixed evenly; 2) the raw materials are mixed into the extruder hopper, while using foaming gas foaming; 3) of the extruder EPE material is shaped by the blower, and received in shape, EPE sheet. The application of the invention can significantly reduce the density of EPE sheet.
【技术实现步骤摘要】
一种EPE片材的制备方法及其制备的产品
本专利技术涉及塑料制造
，特别是涉及一种EPE片材的制备方法及其制备的产品。
技术介绍
EPE(ExpandablePolyethylene)，是可发性聚乙烯，又称珍珠棉，是以低密度聚乙烯(LDPE)为主要原料挤压生成的高泡沫聚乙烯制品。它由低密度聚乙烯脂经物理发泡产生无数的独立气泡构成。是目前世界上比较先进的保护性内包装材料。EPE具有较高的弹性、外观洁白、轻便、灵活、并能弯曲、以吸收撞击力分散外缓冲的效果，克服了普通发泡胶易碎，变形和恢复的缺点，EPE有保温，隔水防潮、隔热、隔音、防摩擦、抗老化、耐腐蚀等特点，且具有很好的加工性。另外，EPE是一种环保材料可以回收的材料，是传统包装材料的理想替代品。EPE在产品包装方面得到广泛的运用，如电脑，电器，高档家私，皮具，手袋，鞋业等，特别是高档工艺品包装，EPE与其它高档装饰布，绒布结合，具有豪华气派，又不失其良好的抗冲击保护效果，也是今后包装高档化发展的趋势。然而，专利技术人在实现本专利技术的过程中发现，利用现有技术制备的EPE片材密度较大的技术问题。
技术实现思路
本专利...
【技术保护点】
一种EPE片材的制备方法，其特征在于，所述方法包括：1)称取原料：聚乙烯胶粒100重量份、成核剂3.2～4.6重量份，优选为3.8～4.1重量份；抗收缩剂0.7～1.5重量份，优选为0.9～1.2重量份；发泡剂5.4～8.3重量份，优选为6.3～7.5重量份；将原料均匀混合；2)将混合后的所述原料加入挤出机料斗内，同时使用发泡气体进行发泡；3)利用鼓风机对挤出机挤出的EPE材料进行定型，并在定型后收料，得到EPE片材。
【技术特征摘要】
1.一种EPE片材的制备方法，其特征在于，所述方法包括：1)称取原料：聚乙烯胶粒100重量份、成核剂3.2～4.6重量份，优选为3.8～4.1重量份；抗收缩剂0.7～1.5重量份，优选为0.9～1.2重量份；发泡剂5.4～8.3重量份，优选为6.3～7.5重量份；将原料均匀混合；2)将混合后的所述原料加入挤出机料斗内，同时使用发泡气体进行发泡；3)利用鼓风机对挤出机挤出的EPE材料进行定型，并在定型后收料，得到EPE片材。2.根据权利要求1所述的EPE片材的制备方法，其特征在于，所述原料还包括抗静电剂，所述抗静电剂的添加量为1.0～3.0重量份，优选为2.1～2.7重量份。3.根据权利要求2所述的EPE片材的制备方法，其特征在于，所述原料还包括增强纤维，所述增强纤维的添加量为5～15重量份，优选为7～12重量份。4.根据权利要求3所述的EPE片材的制备方法，其特征在于，在将所述...
【专利技术属性】
技术研发人员：汪锋，王龙珑，
申请(专利权)人：合肥朗胜新材料有限公司，
类型：发明
国别省市：安徽,34