一种利用尾矿制备泡沫陶瓷的方法技术
A method of making foam ceramics from Tailings
The invention discloses a method for preparing ceramic foam using tailings for the first use of iron tailings 54.5wt.%, 10wt.% sediment of the Yellow River 19.5wt.% waste glass and 15wt.% sodium feldspar as main raw materials, silicon carbide powder using 1wt.% as foaming agent, followed by ball milling and mixing by mixing powder; then to semi dry mixed powder get blank pressing to join the PVA after the blank of granulation; foaming process at 120 DEG C 12h after cooling to obtain iron tailings of ceramic foam after foaming process. The method has the advantages of high solid waste utilization rate and low raw material cost, and the product has uniform pore size distribution and simple preparation process.
【技术实现步骤摘要】
一种利用尾矿制备泡沫陶瓷的方法
本专利技术属于泡沫材料制备领域，具体涉及一种利用尾矿制备泡沫陶瓷的方法。
技术介绍
铁尾矿是目前国内产生量较大的一类工业固体废弃物，大量铁尾矿堆积占用土地，污染地下水，产生灰尘污染，因而对铁尾矿的利用是目前研究较多的一个热点。目前铁尾矿主要利用途径是用来制备耐火材料、玻璃制品、建筑陶瓷制品、水泥、墙体材料等。泡沫陶瓷是一种新型建筑外墙和屋面保温材料，主要原料包括天然矿物和各种固体废弃物，专利CN105367117A公布了一种采用粘土、长石和硅灰石等作为原料制备泡沫陶瓷的方法；专利CN103396157A公布了一种以铁尾矿为主要原料制备泡沫陶瓷轻质墙体建筑材料，其中铁尾矿用量达到了铁尾矿50～55wt.％；专利CN102417368A公布了一种利用高硅铁尾矿制备泡沫陶瓷方法，铁尾矿用量达到了60-70％，配方同时添加量粉煤灰和煤矸石，发泡温度较高，达到了1150-1250℃。专利CN103396157A公布了一种以铁尾矿为主要原料的泡沫陶瓷轻质墙体建筑材料及其生产工艺，从而可以代替传统的墙体材料、保温材料，配方中采用了大量化工原料，例...
【技术保护点】
一种利用尾矿制备泡沫陶瓷的方法，其特征在于，包括以下步骤：步骤一：采用54.5wt.％的铁尾矿，10wt.％黄河泥沙，19.5wt.％废玻璃和15wt.％钠长石为主要原料，采用1wt.％碳化硅粉作为发泡剂，随后采用球磨进行混料得到混合粉料；步骤二：向混合粉料加入PVA造粒后进行半干压成型得到坯体；将坯体在120℃保温12h后进行发泡工艺，发泡工艺结束后冷却即获得铁尾矿泡沫陶瓷。
【技术特征摘要】
1.一种利用尾矿制备泡沫陶瓷的方法，其特征在于，包括以下步骤：步骤一：采用54.5wt.％的铁尾矿，10wt.％黄河泥沙，19.5wt.％废玻璃和15wt.％钠长石为主要原料，采用1wt.％碳化硅粉作为发泡剂，随后采用球磨进行混料得到混合粉料；步骤二：向混合粉料加入PVA造粒后进行半干压成型得到坯体；将坯体在120℃保温12h后进行发泡工艺，发泡工艺结束后冷却即获得铁尾矿泡沫陶瓷。2.根据权利要求1所述的一种利用尾矿制备泡沫陶瓷的方法，其特征在于，步骤一中的混料方式为干法混料。3.根据权利要求1所述的一种利用尾矿制备泡沫陶瓷的方法，其特征在于，步...
【专利技术属性】
技术研发人员：殷海荣，王飞，白建光，张森，陈平，田一冲，汪枫帆，高杨，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：陕西,61