The present invention relates to a paper gold. Paper gold process includes the following steps: firstly, the prepared tissue, and then use the precious metal raw material rolling cut into foil coated adhesive in tissue paper, one side will fit in with the thin foil glue, and then into the oil pressure in the hydraulic press a bright sand surface pattern; or, to prepare a paper, and then use your the metal material rolling cut into foil, then put the oil pressure in the hydraulic press foil a bright sand surface pattern, with viscose in tissue paper, one side will fit in with the thin foil glue, finally into the machine heat meter. The manufacturing process of the invention makes the pattern of bright sand surface by stamping. The viscose is used to ensure that the precious metal foil is firmly adhered to the thin paper, the whole process is simplified, the processing time is less, the production efficiency is improved, and the cost is reduced.
【技术实现步骤摘要】
一种纸贴金工艺
本专利技术涉及贵金属加工技术，尤其涉及一种纸贴金工艺。
技术介绍
薄片类的工艺礼品为了增加本身价值、提高档次，通常会在其上表面加上一层相对较薄的贵金属层(金、银等)作为装饰，譬如金银钞、金银邮票、明信片或者贴金的画等等。现有技术中更多的薄片类工艺品是将贵金属层直接冲压固定在纸基上，并且贵金属层上的图案通过雕刻形成，这样的制作过程相对复杂，加工耗时较多，有待改进。
技术实现思路
本专利技术的目的在于为克服现有技术的缺陷，而提供一种纸贴金工艺，以简化工艺、降低耗时。为实现上述目的，本专利技术采用以下技术方案：一种纸贴金工艺，其包括以下步骤：先备好薄纸，然后用贵金属原材料轧制裁切成箔片，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，然后整体放入油压机中油压出亮砂面图案；或者，先备好薄纸，然后用贵金属原材料轧制裁切成箔片，随后将箔片放入油压机中油压出亮砂面图案，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，最后放入过塑机热表。进一步地，箔片的厚度范围为0.004mm-0.01mm。进一步地，在薄纸上涂抹粘胶的区域形状大小为箔片的形状大小等比例缩小1％。...
【技术保护点】
一种纸贴金工艺，其特征在于，其包括以下步骤：先备好薄纸，然后用贵金属原材料轧制裁切成箔片，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，然后整体放入油压机中油压出亮砂面图案；或者，先备好薄纸，然后用贵金属原材料轧制裁切成箔片，随后将箔片放入油压机中油压出亮砂面图案，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，最后放入过塑机热表。
【技术特征摘要】
1.一种纸贴金工艺，其特征在于，其包括以下步骤：先备好薄纸，然后用贵金属原材料轧制裁切成箔片，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，然后整体放入油压机中油压出亮砂面图案；或者，先备好薄纸，然后用贵金属原材料轧制裁切成箔片，随后将箔片放入油压机中油压出亮砂面图案，在薄纸上涂抹上粘胶，将箔片贴合在薄纸抹胶的一面上，最后放入过塑机热表。2.如权利要求1所述的纸贴金工艺，其特征在于，所述箔片的厚度范围为0.004mm-0.01mm。3.如权利要求1所述的纸贴金工艺，其特征在于，在薄纸上...