一种植物软胶囊外壳材料及其制备方法技术
A kind of plant soft capsule shell material and its preparation method
The invention discloses a plant soft capsule shell material and preparation method thereof; a plant soft capsule shell material, according to the following weight percentage: 40% 50% hydroxypropyl starch, glycerol 10 20% water, 30% 50%; preparation method includes the following steps: step one, feeding and weighing; step two, step three, glue; rolling pill; use a reasonable formula, combined with the processing steps, which has wide adaptability, without cross reaction risk and stability advantages of high plant soft capsule rolling out can be taken together with many drugs, high safety, in the human body can not be absorbed after disintegration with, excreta excreted in high humidity storage conditions, the index of plant soft capsule compared to soft gelatin capsules has more advantages, but also suitable for vegetarians take.
【技术实现步骤摘要】
一种植物软胶囊外壳材料及其制备方法
本专利技术涉及功能性食品制备
，具体而言，涉及一种非明胶软胶囊外壳材料，安全可靠的植物软胶囊外壳材料及其制备方法。
技术介绍
软胶囊发展至今品种多样，其中明胶软胶囊是现阶段软胶囊市场中应用最为广泛的一种；因为明胶可掩盖许多药物的气味、口感和对胃的刺激性，故很快被推广应用于各种固体制剂的生产中；随着人们生活水平的提高，明胶软胶囊储存性较差、易变形、以及不能被犹太人、清真穆斯林或素食主义者接受等缺点越专利技术显，加之90年代以来英国疯牛病的爆发，其事件波及到明胶市场；这给当前明胶软胶囊产业造成冲击，严重阻碍软胶囊的发展；因此，开专利技术胶替代物来制备新型的植物软胶囊受到广大研究人员的高度重视。植物软胶囊是以来源于天然植物的植物纤维素或水溶性多糖为原料，其胶料多以天然、半合成及合成物质来代替明胶，能有效避免疯牛病的传播及毒胶囊事件的发生，且能满足素食主义者等要求，因此被认为是近年来药用辅料研究的热点；在产品特性上，跟传统明胶软胶囊相比，植物软胶囊的热稳定性能更加优秀，即使超过50℃的环境，也能维持完整的外形，不变形，不粘丸，降低...
【技术保护点】
一种植物软胶囊外壳材料；其特征是：按以下重量百分比计：羟丙基淀粉40%‑50%，甘油10‑20%，水30%‑50%。
【技术特征摘要】
1.一种植物软胶囊外壳材料；其特征是：按以下重量百分比计：羟丙基淀粉40%-50%，甘油10-20%，水30%-50%。2.根据权利要求1所述的一种植物软胶囊外壳材料的制备方法，其特征是：主要包括以下步骤：步骤一、配料和称量；步骤二、化胶；步骤三、轧丸。3.根据权利要求2所述的一种植物软胶囊外壳材料的制备方法，其特征是：所述的步骤一，按照批生产量及产品配方，准确称取本批所需的原料、辅料并由专人复核，物料使用前应核对所称原料的品名、检验单号、批号及重量是否与批记录相一致，确...
【专利技术属性】
技术研发人员：陈铖，夏旭东，张国栋，张兴，张涛，张勇，
申请(专利权)人：江苏艾兰得营养品有限公司，
类型：发明
国别省市：江苏,32