The invention relates to a bubble gum paste can eliminate U type adhesive method, which comprises the following steps: Step 1: adhesive surface treatment; step 2: Step 3: adhesive; bonding; step 4: pressurized curing: in parts bonding area is made on the surface of the vacuum bag and vacuum, and then send into the hot pot, heating and pressurizing, curing; step 5: cleaning and inspection. The invention is verified by the bonding peel strength test and the parts percussion check. It is a bonding method of quality, safety and reliability in the field of composite adhesives, and it is simple and convenient to operate. It effectively eliminates bubbles generated during bonding and significantly improves the bonding quality of U parts.
【技术实现步骤摘要】
一种可以排除糊状胶气泡的U型件胶接方法
本专利技术是一种U型件使用糊状胶胶接时排除气泡的胶接工艺方法，属于复合材料胶接领域、涉及一种排除气泡的U型件胶接工艺方法。
技术介绍
零件的U型部位与U型件需要使用糊状胶胶接时，糊状胶受热后内部易形成气泡，由于U型件均匀受压时，胶接区域的边缘易闭合，导致气泡很难从U型件的边缘排出，零件胶接固化后在胶接面就形成了大面积的无规律分布的气泡，导致零件敲击检测异常。
技术实现思路
本专利技术的目的是：提供一种质量安全可靠、操作简便可行的可以排除糊状胶气泡的U型件胶接工艺方法。本专利技术的技术方案是，一种可以排除糊状胶气泡的U型件胶接方法,包括以下步骤：步骤1：胶接面处理1)使用细砂纸将零件U型部位外表面的胶接区打磨粗糙；2)使用酒精或者丙酮将零件U型部位外表面的胶接区清洗干净并晾干；3)使用酒精或者丙酮将锦纶网清洗干净并晾干；步骤2：配胶1)按糊状胶胶液组分配置比例称取适量的胶液；2)使用调胶杯和调胶棒将胶液搅拌均匀；步骤3：胶接1)将配制好的糊状胶胶液均匀的涂抹在零件U型部位外表面的胶接区；2)将裁剪的整张的锦纶网均匀的铺贴在零件U型...
【技术保护点】
一种可以排除糊状胶气泡的U型件胶接方法,包括以下步骤：步骤1：胶接面处理1)使用细砂纸将胶接面打磨粗糙；2)使用酒精或者丙酮将胶接面清洗干净并晾干；3)使用酒精或者丙酮将锦纶网清洗干净并晾干；步骤2：配胶1)按糊状胶胶液组分配置比例称取适量的胶液；2)使用调胶杯和调胶棒将胶液搅拌均匀；步骤3：胶接1)将配制好的糊状胶胶液均匀的涂抹在零件U型部位胶接区的外表面；2)将裁剪的整张的锦纶网均匀的铺贴在零件U型部位的胶接区的外表面，要求无皱褶、无对接和无搭接；3)将配制好的糊状胶胶液均匀的锦纶网的外表面，要求无漏涂区域、无富胶区域；4)将U型件安装到U型部位的胶接区上，要求比对后一...
【技术特征摘要】
1.一种可以排除糊状胶气泡的U型件胶接方法,包括以下步骤：步骤1：胶接面处理1)使用细砂纸将胶接面打磨粗糙；2)使用酒精或者丙酮将胶接面清洗干净并晾干；3)使用酒精或者丙酮将锦纶网清洗干净并晾干；步骤2：配胶1)按糊状胶胶液组分配置比例称取适量的胶液；2)使用调胶杯和调胶棒将胶液搅拌均匀；步骤3：胶接1)将配制好的糊状胶胶液均匀的涂抹在零件U型部位胶接区的外表面；2)将裁剪的整张的锦纶网均匀的铺贴在零件U型部位的胶接区的外表面，要求无皱褶、无对接和无搭接；3)将配制好的糊状胶胶液均匀的锦纶网的外表面，要求无漏涂区域、无富胶区域；4)将U型件安装到U型部位的胶接区上，要求比对后一次安装到位；5)使用胶带将两者固定；步骤4：...