The invention provides a preparation method of high transparent and high impact polypropylene resin, which includes mixing polypropylene resin and several auxiliaries and melting granulation to obtain polypropylene resin products. Random copolymer resin for ethylene and propylene, ethylene content of 3 5wt%, melt flow rate of 0.1 2.0g/10min. The additives include transparent nucleating agent, halogen absorbent, antioxidant A and antioxidant B. The advantage of the invention is that the polypropylene has high transparency and high constant low temperature impact strength, which is suitable for the preparation of hollow blow molding products and plastic sheet and sheet material.
【技术实现步骤摘要】
适合吹塑工艺的高透明高抗冲聚丙烯树脂
本专利技术涉及吹塑材料领域，具体地，涉及一种高透明高抗冲聚丙烯树脂制备方法，该聚丙烯特别适用于透明中空吹塑制品和吸塑成型板材及片材。背景内容聚乙烯(PE)是塑料中空吹塑成型材料中最早实现商品化生产的品种，也是发展最快、应用最广的品种，目前，以PE为原料生产的中空制品的产量占到世界挤出吹塑制品总产量约三分之二。普通聚丙烯(PP)的熔体强度较低，吹塑过程中抗熔垂性能较差，因此应用于中空制品方面的研究很少。此外，市场上很多中空制品对其透明性要求较高，而聚乙烯类的树脂吹塑植被的中空制品透明度无法达到高品质产品的要求。除此之外，下游制品对原料的冲击性能要求越来越高，要求制品满足常低温跌落试验要求。因此，研究开发高透明高抗冲的聚丙烯专用料具有一定的潜在市场价值和前景。
技术实现思路
本专利技术提供了一种高透明高抗冲聚丙烯树脂制备方法，它所要解决的技术问题是通过调整聚丙烯树脂基料的分子量，同时改善树脂的熔体强度、延展流动性和透明性，进一步地通过控制乙烯含量满足原料常低温冲击性能要求，从而克服现有热成型设备成型聚丙烯制品的技术缺陷，制备高透明...
【技术保护点】
一种高透明高抗冲聚丙烯树脂，其特征在于：将包含有如下质量份数比的组分混合均匀后进行熔融造粒获得；
【技术特征摘要】
1.一种高透明高抗冲聚丙烯树脂，其特征在于：将包含有如下质量份数比的组分混合均匀后进行熔融造粒获得；2.如权利要求1所述的一种高透明高抗冲聚丙烯树脂，其特征在于：所述聚丙烯树脂基料为丙烯和碳原子数不大于8的烯烃中的一种或几种的无规共聚产物中的一种或几种；其中，所述丙烯的用量为聚丙烯树脂基料总重量的80-95％。3.如权利要求1所述的一种高透明高抗冲聚丙烯树脂，其特征在于：所述聚丙烯树脂基料为丙烯和乙烯的无规共聚物；其中，乙烯的含量为3-5wt％。4.如权利要求1所述的一种高透明高抗冲聚丙烯树脂，其特征在于：所述聚丙烯树脂基料的基料熔体流动速率为0.1-2.0g/10min。5.如权利要求1所述的一种高透明高抗冲聚丙烯树脂，其特征在于：所述聚丙烯树脂基料的基料熔体流动速率1.0-1.5g/10min。6.如权利要求1所述的一种高透明高抗冲聚丙烯树脂，其特征...
【专利技术属性】
技术研发人员：丁士琪，
申请(专利权)人：上海帆顺包装集团有限公司，
类型：发明
国别省市：上海,31