用于二次电池的隔膜制造技术
A diaphragm for two batteries
This paper provides a diaphragm for an electrochemical device (such as a lithium ion battery). The porous protective layer on the surface of the one or two diaphragm is disclosed comprising a porous base material coated porous substrate and disclosed in this paper, the protective layer comprises a porous organic binder and inorganic filler, and the inorganic filler selected from Al2O3, SiO2, including TiO2, ZrO2, BaOx, ZnO, CaCO3, TiN, AlN, MTiO3, K2O, nTiO2, Na2O, mTiO2 and the combination of the group composed of whisker material, wherein X is 1 or 2; M is Ba, Sr or Ca; n is 1, 2, 4, 6 or 8; and M is 3 or 6. The diaphragm disclosed in this paper has excellent safety, ion transmittance and cycle performance.
【技术实现步骤摘要】
用于二次电池的隔膜
本技术涉及用于电化学装置(例如锂离子电池)的隔膜。更具体地，本技术涉及一种隔膜，其中在多孔性基底材料的一个或两个表面上形成由有机粘结剂和无机填料的混合物制成的保护性多孔层。
技术介绍
锂离子电池(LIB)已经广泛用于各种应用，尤其是例如笔记本电脑、移动电话和数码相机等消费类电子产品。最近，锂离子电池由于其优越的能量和功率密度，已经开始在汽车中使用。LIB通常包括阳极、阴极、隔膜和电解液。为了防止短路，同时保持离子导电性，阳极和阴极通过隔膜彼此隔开。隔膜通常是薄的、多孔的电绝缘材料，其具有高的离子透过率、良好的机械强度以及对系统中使用的化学制品和溶剂的长久稳定性，例如电化学电池的电解液。由于大量的能量储存在完全充电状态下的电池中，因此在高性能电池系统中使用的隔膜必须安全。在电池故障(例如过度充电或短路)的情况下，这些能量不能以不受控制的方式释放，因为这会导致电池的爆炸或点燃。通常，一个典型的有机隔膜由包括聚烯烃基基底和无机涂层的复合膜组成。这些聚烯烃基隔膜的主要的缺点是低热稳定性极限。当电池的温度超过150℃或更低时，有机隔膜迅速收缩。阴极和阳极...
【技术保护点】
一种二次电池的隔膜，包含多孔性基底材料，以及涂覆在所述多孔性基底材料的一个表面上的保护性多孔层，其中所述保护性多孔层包含有机粘结剂和无机填料，其中所述无机填料为晶须型材料，其中所述晶须型材料的直径是0.05μm至3μm，以及平均长度是0.05μm至30μm，其中所述晶须型材料具方向性地分布在整个所述保护性多孔层中，且所述晶须型材料倾向于沿着TD方向排列，且其中所述隔膜的厚度是1μm至80μm，以及孔隙率是40％至97％。
【技术特征摘要】
2016.05.25 US 62/341,0791.一种二次电池的隔膜，包含多孔性基底材料，以及涂覆在所述多孔性基底材料的一个表面上的保护性多孔层，其中所述保护性多孔层包含有机粘结剂和无机填料，其中所述无机填料为晶须型材料，其中所述晶须型材料的直径是0.05μm至3μm，以及平均长度是0.05μm至30μm，其中所述晶须型材料具方向性地分布在整个所述保护性多孔层中，且所述晶须型材料倾向于沿着TD方向排列，且其中所述隔膜的厚度是1μm至80μm，以及孔隙率是40％至97％。2.如权利要求1所述的二次电池的隔膜，其中所述晶须型材料的长度与直径比是5至300。3.如权利要求1所述的二次电池的隔膜，其中至少50％的所述晶须型材料处于围绕TD方向的轴线的±...