The invention discloses a preparation method of electromagnetic shielding polyethylene film, characterized by comprising the following steps: (1) low density polyethylene, carbon fiber, carbon black mixed according to a certain proportion, with a mixture; (2) to the step (1) mixed organic solvent used to dissolve the material is added while heating, stirring evenly to obtain evenly mixed material; (3) the step (2) was prepared by mixing cast on a substrate 50~60 in constant temperature drying box, get the film. The method of the invention not only has short preparation time and low cost, but also has high strength of the prepared film.
【技术实现步骤摘要】
一种电磁屏蔽聚乙烯薄膜的制备方法
本专利技术属于聚乙烯薄膜制备的
，尤其涉及一种电磁屏蔽聚乙烯薄膜及其制备方法。
技术介绍
随着电子工业的高速发展，各种民用和军用的电子产品数量急剧增加，电磁干扰(EMI)已经成为一种社会公害。因此，制备一种具有电磁屏蔽功能的薄膜，具有重要意义。而现有的电磁屏蔽薄膜通常强度不高，或者价格昂贵。本专利技术目的在于研发一种具有有效电磁屏蔽功能且工艺简单的电磁屏蔽聚氧乙烯薄膜的制备方法。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种电磁屏蔽聚乙烯薄膜及其制备方法。该方法不仅制备消耗时间短，而且制备得到的薄膜强度高。本专利技术提出一种电磁屏蔽聚乙烯薄膜及其制备方法，包括以下步骤：(1)将低密度聚乙烯、碳纤维、炭黑按照一定比例混合，配合成混合料；(2)向所述步骤(1)混料中添加用于溶解的有机溶剂，边加热边搅拌均匀，得到均匀的混料；(3)将所述步骤(2)制备得到的混料流延于一基底上，50～60℃恒温箱干燥，得到所述薄膜。进一步的，所述步骤(1)中低密度聚乙烯、碳纤维、炭黑的混合比例按照重量份数计算为100:30:30。进一步的，所述步骤(3)中，所述干燥温度为55℃。进一步的，所述步骤(3)中，所述薄膜厚度为20微米。本专利技术与现有技术相比，具有以下有益效果：本专利技术方法不仅制备消耗时间短，成本低，而且制备得到的薄膜强度高。具体实施方式下面结合具体实施例对本专利技术作进一步解说。实施例1将100kg低密度聚乙烯、30kg碳纤维、30kg炭黑混合，配合成混合料；向所述混料中添加用于溶解的有机溶剂，边加热边搅拌均匀，...
【技术保护点】
一种电磁屏蔽聚乙烯薄膜的制备方法，其特征在于，包括以下步骤：(1)将低密度聚乙烯、碳纤维、炭黑按照一定比例混合，配合成混合料；(2)向所述步骤(1)混料中添加用于溶解的有机溶剂，边加热边搅拌均匀，得到均匀的混料；(3)将所述步骤(2)制备得到的混料流延于一基底上，50～60℃恒温箱干燥，得到所述薄膜。
【技术特征摘要】
1.一种电磁屏蔽聚乙烯薄膜的制备方法，其特征在于，包括以下步骤：(1)将低密度聚乙烯、碳纤维、炭黑按照一定比例混合，配合成混合料；(2)向所述步骤(1)混料中添加用于溶解的有机溶剂，边加热边搅拌均匀，得到均匀的混料；(3)将所述步骤(2)制备得到的混料流延于一基底上，50～60℃恒温箱干燥，得到所述薄膜。2.根据权利要求1所述的一种电磁屏蔽聚乙烯薄膜的制备方法，其特征在于，所述步骤(...
【专利技术属性】
技术研发人员：林成辉，
申请(专利权)人：清远市百悦企业服务有限公司，
类型：发明
国别省市：广东,44