The invention relates to an inorganic zinc rich coating with aluminum silicate fiber and its preparation process. Because of the poor uniformity of coating uniformity in the coating process of ordinary zinc powder, the effect of coating is reduced. In order to improve the coating performance, the zinc powder mixture added with aluminum silicate fiber is added to the zinc powder by adding aluminum silicate fiber filler, and then added to the coating to improve the coating uniformity of the coating process. The process is simple and the operation is strong.
【技术实现步骤摘要】
一种添加硅酸铝纤维的无机富锌涂料及其制备方法
本专利技术涉及一种涂料,特别涉及一种添加硅酸铝纤维的水性无机富锌涂料及其制备方法,属于涂料加工领域。
技术介绍
全世界每年因钢铁腐蚀造成的经济损失约占各国GDP的2%-4%,因腐蚀而报废的金属达亿吨以上。人们通过各种方式来延缓钢铁的腐蚀速度,如改进基材、增加金属镀层、添加缓蚀剂等,虽然对腐蚀具有一定的延缓效果,但在含盐的环境如海水或高温/高湿环境中,镀有金属的表面会形成一些其他的锈迹,导致基材表面明显恶化的外观或防锈能力的降低。而在金属表面涂有一层防腐涂料,则可起到较好的防腐作用。富锌防腐涂料被广泛使用,富锌防腐涂料不但能隔绝空气,而且能形成原电池保护。富锌防腐涂料分为有机富锌防腐涂料和无机富锌防腐涂料,有机富锌涂料常用环氧树脂、氯化橡胶、乙烯基树脂和聚氨酯树脂为成膜基料。但有机富锌涂料的有机成膜物的导电性能差。无机富锌涂料又分为有溶剂型和水性两类。其中水性无机富锌涂料是由水性无机硅酸盐(纳、钾、锂)树脂、锌粉、助剂等组成。水性无机富锌底漆以其独特的保护机理、优异的防腐性能,同时具有零挥发性有机化合物(VOC)排放、配套性良好和价格合理而被广泛应用,成为建筑钢结构等基体的主要底漆。但由于锌粉混合在硅酸盐水性无机富锌涂料中,涂层均匀性差,从而导致涂料涂层发生开裂现象。为了提高涂层柔韧性,抗开裂,在锌粉中添加硅酸铝纤维填料,制备锌粉混合物,再添加到涂料中,提高涂料的综合性能。
技术实现思路
为了提高涂层柔韧性,抗开裂,制备一种高质量的无机富锌涂料,该涂料包括以下质量份数的原料:硅酸钠溶液5%-10%;硅酸钾溶液5%-1 ...
【技术保护点】
一种添加硅酸铝纤维的无机富锌涂料,其特征在于该涂料包括以下质量份数的原料:硅酸钠溶液 5%;硅酸钾溶液 5%;水 20%铝改性硅溶胶 34.5%三甲基苄基氢氧化铵催化剂 0.5%十二烷基二醇酰胺 5%钛酸四异丙酯 5%硅丙乳液 5%含氧化锆纤维的锌粉混合物 19%脲醛‑聚氨酯树脂 1% 。
【技术特征摘要】
1.一种添加硅酸铝纤维的无机富锌涂料,其特征在于该涂料包括以下质量份数的原料:硅酸钠溶液5%;硅酸钾溶液5%;水20%铝改性硅溶胶34.5%三甲基苄基氢氧化铵催化剂0.5%十二烷基二醇酰胺5%钛酸四异丙酯5%硅丙乳液5%含氧化锆纤维的锌粉混合物19%脲醛-聚氨酯树脂1%。2.根据权利要求1所述的一种添加硅酸铝纤维的无机富锌涂料,其特征在于,硅酸钠溶液中,硅酸钠溶液的质量百分比浓度选为3%-6%。3.根据权利要求1所述的一种添加硅酸铝纤维的无机富锌涂料,其特征在于,硅酸钾溶液中,硅酸钾溶液的质量百分比浓度选为3%-6%。4.根据权利要求1所述的一种添加硅酸铝纤维的无机富锌涂料,其特征在于,所述的铝改性硅溶胶中铝离子的摩尔含量选为1%-2%。5.根据权利要求1所述的一种添加硅酸...