本发明专利技术提供一种防晒隔热塑料编织袋用原料配方，按重量由下述组分组成：聚丙烯80‑120份；低密度聚乙烯40‑60份；酚醛树脂22‑26份；添加母料4‑8份；聚磷酸铵1‑1.2份；纳米石墨0.5‑0.8份；紫外线吸收剂5‑7份；改性添加剂15‑25份；拟除虫菊酯0.2‑0.4份；助剂3‑3.5份。本发明专利技术添加的助剂能够有效的抗老化、防日晒，且隔热效果好，而且拟除虫菊酯的添加还能有效的防虫咬，延长了包装袋的使用寿命，使用效果更好。

Raw material formula for sunscreen heat insulation plastic woven bag

The invention provides a sunscreen insulation plastic raw material formula for woven bag, comprising the following components by weight: 80 polypropylene 120; low density polyethylene 40 60 22 26; phenolic resin; add 4 masterbatch 8; ammonium polyphosphate 1 1.2; 0.5 0.8 nano graphite 5 7; UV absorber; modifier 15 25; pyrethroid 0.2 0.4; 3 3.5 auxiliaries. The additive can effectively resist aging and sunlight, and has good heat insulation effect. Moreover, the addition of pyrethroid can effectively prevent insect bites, prolong the service life of the packaging bag and improve the use effect.

【技术实现步骤摘要】
一种防晒隔热塑料编织袋用原料配方
本专利技术涉及编织袋生产
，尤其涉及一种防晒隔热塑料编织袋用原料配方。
技术介绍
塑料编织袋的主要原料成分为聚丙烯和聚乙烯，目前广泛应用于水泥、肥料、化工等领域。其主要生产工艺是利用原料经过挤出薄膜、拉丝、收卷、圆织、印刷、裁割、缝纫，最终得到塑料编织袋成品。传统的编织袋生产材料都是聚丙烯、聚乙烯加添加母料干燥搅拌混合制得，生产出的塑料编织袋在夏季高温和紫外线照射下容易老化、起皮、断裂、粉碎，不但影响塑料袋内的物品，还影响了塑料编织袋的使用效果。
技术实现思路
本专利技术正是针对以上技术问题，提供一种防晒隔热塑料编织袋用原料配方。本专利技术为实现上述目的，采用以下技术方案：一种防晒隔热塑料编织袋用原料配方，其特征在于，按重量由下述组分组成：所述添加母料为纳米碳酸钙、氧化钡、蛭石按重量比3:2:1的比例混合研磨制得的混合物。所述改性添加剂由下列重量份的原料组成：改性高岭土40-50份、聚乳酸15-18份、氯化钠8-13份、聚乙交酯1-3份、氧化铝2-3份、石英粉1-3份。所述助剂由下列重量份的原料组成：粘土20-24份、明矾5-6份、促进剂DM2-3本文档来自技高网...

【技术保护点】
一种防晒隔热塑料编织袋用原料配方，其特征在于，按重量由下述组分组成：

【技术特征摘要】
1.一种防晒隔热塑料编织袋用原料配方，其特征在于，按重量由下述组分组成：2.根据权利要求1所述的一种防晒隔热塑料编织袋用原料配方，其特征在于，所述添加母料为纳米碳酸钙、氧化钡、蛭石按重量比3:2:1的比例混合研磨制得的混合物。3.根据权利要求1所述的一种防晒隔热塑料编织袋用原料配方，其特征在于，所述改性添加剂由下列重量份的原料组成：改性高岭土40-50份、聚乳酸15-18份、氯化钠8-13份、聚乙交酯1-3份、氧...

【专利技术属性】
技术研发人员：王旭辉，
申请(专利权)人：天津市旭辉恒远塑料包装股份有限公司，
类型：发明
国别省市：天津,12