The invention discloses a fluorinated hydrophobic anti leakage medical bag material, which is composed of the following raw materials in weight portion: 16 fluorinated monomer 20, zirconia 6 9, 2, 1 itaconic acid sebacic acid octyl two 3 4, polyethylene glycol 1000 3 lauryl methyl two, 4 0.5 amine oxide 1, benzo triazole three 0.7 1, 3 4, ammonium polyphosphate PVC 120 140, Ding Ji 1, 0.8 mercaptan tin peroxide cumene two 1 2, the invention can effectively improve the zirconia dispersion in polyester compatibility, improve the stability of product strength the invention adopts the fluorine modified monomer, can effectively improve the hydrophobic properties of the finished material.
【技术实现步骤摘要】
一种氟化疏水抗渗漏医用袋材料及其制备方法
本专利技术属于材料领域，具体涉及一种氟化疏水抗渗漏医用袋材料及其制备方法。
技术介绍
医用聚氯乙烯是由氯乙烯在引发列作用下聚合而成的热塑性树脂。平均聚合度为5001-14001，不溶于水，可溶于有机溶剂如环己酮、四氢吠喃等。耐热性不高，一般应在70℃以下使用。医用聚氯乙烯要求其制品呈微黄色、透明、柔软，具有一定的抗凝血性和曲挠性，主要用作输血、输液袋，体外循环装置导管，鼓泡式氧合袋，尿袋等与人体短期接触的制品。然而目前市售的医用聚氯乙烯材料在低温下容易逐渐变硬，长期使用会老化而变脆、变黄，并伴有增塑剂向表面迁移的"起霜"现象。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种氟化疏水抗渗漏医用袋材料及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种氟化疏水抗渗漏医用袋材料，它是由下述重量份的原料组成的：氟化单体16-20、氧化锆6-9、衣康酸1-2、葵二酸二辛酯3-4、聚乙二醇10003-4、月桂基二甲基氧化胺0.5-1、苯骈三氮唑0.7-1、聚磷酸铵3-4、聚氯乙烯120-140、丁基硫醇锡0...
【技术保护点】
一种氟化疏水抗渗漏医用袋材料，其特征在于，它是由下述重量份的原料组成的：氟化单体16‑20、氧化锆6‑9、衣康酸1‑2、葵二酸二辛酯3‑4、聚乙二醇1000 3‑4、月桂基二甲基氧化胺0.5‑1、苯骈三氮唑0.7‑1、聚磷酸铵3‑4、聚氯乙烯120‑140、丁基硫醇锡0.8‑1、过氧化二异丙苯1‑2。
【技术特征摘要】
1.一种氟化疏水抗渗漏医用袋材料，其特征在于，它是由下述重量份的原料组成的：氟化单体16-20、氧化锆6-9、衣康酸1-2、葵二酸二辛酯3-4、聚乙二醇10003-4、月桂基二甲基氧化胺0.5-1、苯骈三氮唑0.7-1、聚磷酸铵3-4、聚氯乙烯120-140、丁基硫醇锡0.8-1、过氧化二异丙苯1-2。2.根据权利要求1所述的一种氟化疏水抗渗漏医用袋，其特征在于，所述的氟化单体是由下述重量份的原料组成的：六氟乙酰丙酮0.1-0.2、硼砂3-5、甲基丙烯酸甲酯8-10、甲基硫醇锡0.7-1、n-甲基吡咯烷酮10-13。3.根据权利要求2所述的一种氟化疏水抗渗漏医用袋材料，其特征在于，所述的氟化单体的制备方法包括以下步骤：取六氟乙酰丙酮、甲基硫醇锡混合，在50-60℃下保温搅拌10-20分钟，加入到n-甲基吡咯烷酮中，搅拌均匀，加入硼砂，升高温度为80-90℃，保温搅拌4-10分钟，加入甲基丙烯酸甲酯，搅拌至常温，得所述氟化单体。4.一种如权利要求1-3...
【专利技术属性】
技术研发人员：吴代斌，
申请(专利权)人：安徽省健源医疗器械设备有限公司，
类型：发明
国别省市：安徽,34