The invention relates to a fireproof board, characterized in that, including fire plate body, the inside of the fire board body filled by fireproof filler, the exterior of the fireproof plate body is coated with amino resin fire-retardant coating; the flame retardant filler composition according to the quality of a number are as follows: 15 polyvinyl alcohol 25, glass fiber 10 30 copies, 20 copies, 10 polystyrene calcium carbonate 6 8. The raw material of the invention is reasonable, the raw material is cheap and easy to get, the toughness, the plasticity and the fire resistance of the product are improved, the raw material is easy to be obtained, the price is low, and the processing is simple.
【技术实现步骤摘要】
一种新型防火板
本专利技术涉及一种建筑材料，特别涉及一种新型防火板。
技术介绍
近年来随着建筑行业的飞速发展，火灾的防控也面临巨大的挑战，防火的重要性不言而喻，防火板作为最有效的防火结构，可以对火势进行有效的阻燃，防止进一步蔓延，可以有效的减少火灾对人民生命和财产造成的威胁。
技术实现思路
本专利技术针对上述问题提出了一种新型防火板。具体的技术方案如下：一种新型防火板，其特征在于，包括防火板本体，所述防火板本体内部填充由防火填料，所述防火板本体外部还涂覆有氨基树脂防火涂层；所述防火填料组成成分按质量份数计如下：聚乙烯醇15-25份、玻璃纤维10-30份、聚苯乙烯10-20份、碳酸钙6-8份。上述一种新型防火板，其特征在于，玻璃纤维目数为300目。本专利技术的有益效果为：本专利技术原料配比合理，原料价廉且易得，提高产品韧性、可塑性和防火性，原料易得，价格低廉，加工简单。具体实施方式为使本专利技术的技术方案更加清晰明确，下面对本专利技术进行进一步描述，任何对本专利技术技术方案的技术特征进行等价替换和常规推理得出的方案均落入本专利技术保护范围。实施例1一种新型防火板，其特征在于，包括防火板本体，所述防火板本体内部填充由防火填料，所述防火板本体外部还涂覆有氨基树脂防火涂层；所述防火填料组成成分按质量份数计如下：聚乙烯醇25份、玻璃纤维30份、聚苯乙烯20份、碳酸钙8份。实施例2一种新型防火板，其特征在于，包括防火板本体，所述防火板本体内部填充由防火填料，所述防火板本体外部还涂覆有氨基树脂防火涂层；所述防火填料组成成分按质量份数计如下：聚乙烯醇15份、玻璃纤维10份、聚...
【技术保护点】
一种新型防火板，其特征在于，包括防火板本体，所述防火板本体内部填充由防火填料，所述防火板本体外部还涂覆有氨基树脂防火涂层；所述防火填料组成成分按质量份数计如下：聚乙烯醇15‑25份、玻璃纤维10‑30份、聚苯乙烯10‑20份、碳酸钙6‑8份。
【技术特征摘要】
1.一种新型防火板，其特征在于，包括防火板本体，所述防火板本体内部填充由防火填料，所述防火板本体外部还涂覆有氨基树脂防火涂层；所述防火填料组成成分按质量份数计如...
【专利技术属性】
技术研发人员：吴江，陈秀兰，
申请(专利权)人：镇江泽枫霖建筑材料有限公司，
类型：发明
国别省市：江苏,32