The invention discloses a polycarbonate modified cable material and a preparation method thereof. The material comprises the following raw materials by weight: 10 prepared 18 copies of the ceramic particles, 0.001 graphene, 0.003 copies of 15 copies of the 12 modifier, 30 45 copies of the 50 polycarbonate, polyvinyl butyral 0.3, 65 copies of the coupling agent, 0.8 copies of 0.5 copies of the 0.3 crosslinking agent; after modification of ceramic particles added to polycarbonate and mixing modification, improve the wear resistance of polycarbonate, and retain good machinability, the sheath material for polycarbonate cable, cable in high wear can significantly increase the service life of the environment.
【技术实现步骤摘要】
一种聚碳酸酯改性电缆材料及其制备方法
本专利技术涉及电缆材料领域，具体涉及一种聚碳酸酯改性电缆材料及其制备方法。
技术介绍
电缆是用一根或多根导线经过绞合制作成导体线芯，再在导体上施以相应的绝缘层，外面包上密封护套而形成的导线，主要由线芯、绝缘层、屏蔽层和护套层构成。电缆具有占用地面和空间少；供电安全可靠，触电可能性小；有利于提高电力系统的功率因数；运行、维护工作简单方便；有利于美化城市，具有保密性等诸多优点，被广泛应用于生活和生产中的各个领域。电缆护套层的作用是密封保护电缆免受外界杂质和水分的侵入，防止外力直接损坏电缆绝缘层。电缆护套层材料不仅要求密封性好、防腐性高、机械强度高、阻燃性好，还应当具有一定的耐磨性。聚碳酸酯材料也可作为电缆护套层材料，但聚碳酸酯耐磨性差，用于电缆护套层后，电缆不适合在高磨损环境中长期使用。因此，现有技术中采用了多种改性方法来提高聚碳酸酯材料的耐磨性，如：添加耐磨的无机材料、对聚碳酸酯进行交联、参杂耐磨树脂材料等方法，但由于原材料选择的针对性差或聚碳酸酯聚合度没进行控制等，造成得到的聚碳酸酯材料要么耐磨性达不到要求，要么耐磨性高却加工...
【技术保护点】
一种聚碳酸酯改性电缆材料，其特征在于，包括以下重量份原材料制备而成：10‑18份的陶瓷颗粒、0.001‑0.003份的石墨烯，12‑15份的改性剂、30‑45份的聚乙烯醇缩丁醛、50‑65份的聚碳酸酯、0.3‑0.8份的偶联剂、0.3‑0.5份的交联剂；所述的改性剂为聚丙烯酸酯与正硅酸乙酯组成的混合物；所述的聚乙烯醇缩丁醛聚合度为230‑360；所述的聚碳酸酯聚合度为1200‑1800；所述的偶联剂为甲基丙烯酰氧基丙基三甲氧基硅烷偶联剂；所述的交联剂为2,5‑二甲基‑2,5二叔丁基过氧化己烷。
【技术特征摘要】
1.一种聚碳酸酯改性电缆材料，其特征在于，包括以下重量份原材料制备而成：10-18份的陶瓷颗粒、0.001-0.003份的石墨烯，12-15份的改性剂、30-45份的聚乙烯醇缩丁醛、50-65份的聚碳酸酯、0.3-0.8份的偶联剂、0.3-0.5份的交联剂；所述的改性剂为聚丙烯酸酯与正硅酸乙酯组成的混合物；所述的聚乙烯醇缩丁醛聚合度为230-360；所述的聚碳酸酯聚合度为1200-1800；所述的偶联剂为甲基丙烯酰氧基丙基三甲氧基硅烷偶联剂；所述的交联剂为2,5-二甲基-2,5二叔丁基过氧化己烷。2.根据权利要求1所述的聚碳酸酯改性电缆材料，其特征在于，所述的石墨烯重量份为0.002份。3.根据权利要求1所述的聚碳酸酯改性电缆材料，其特征在于，所述的陶瓷颗粒粒径为0.01-2μm。4.根据权利要求1所述的聚碳酸酯改性电缆材料，其特征在于，所述的陶瓷颗粒为氧化硅陶瓷、氮化硅陶瓷、碳化硅陶瓷中的一种或多...
【专利技术属性】
技术研发人员：舒春柳，
申请(专利权)人：四川力智久创知识产权运营有限公司，
类型：发明
国别省市：四川,51