The invention provides a 5005H34 aluminum alloy sheet and a production method. The Aluminum Alloy plate components: as mass fraction, Si = 0.2%, Fe = 0.55%, Cu = 0.15%, Mn = 0.2%, Mg 0.75~1.0%, Cr = 0.1%, Zn = 0.2%, Ti 0.01~0.05%, other single impurity is less than 0.05%, all the total impurity is less than 0.15%, the rest is Al. The production process includes: Casting sawing milling hot rolling cold rolling ingot heating cleaning baking crosscutting. The production method can ensure the performance of products and shorten the production process. Through hot rolling and 1 pass cold rolling control mechanical properties, the thickness of 2.0~3.0mm plate is produced, which saves 5005H34 cost.
【技术实现步骤摘要】
一种5005H34铝合金板材及其生产方法
本专利技术属于铝合金制造
，具体是涉及一种5005H34铝合金板材及其生产方法。
技术介绍
5005铝合金是Al~Mg系合金中应用较为广泛的一种合金，其板板材系列产品强度适中，具有良好的抗蚀性，熔接性，易加工成形，同时其阳极氧化膜明亮美观。不同热处理状态的5005铝合金板材广泛应用于导体、炊具、仪表板、壳与建筑装饰件，建材内外装材、车辆内装材等方面，其中H34状态板材是其中用量和使用范围最大的一种，市场前景广阔。目前5005H34铝合金板材的工艺流程为：熔铸—锯切—铸锭加热—热轧—冷轧—中间退火—成品冷轧—成品稳定化退火—精整—包装，该流程工艺冗长，加工成本高。同时，为确保中间退火和成品退火性能，热轧后的厚度要为冷轧保留足够的加工空间，热轧厚度较大，效率低；采用成品退火工艺时对退火温度要求苛刻，性能波动大，控制成本高。
技术实现思路
本专利技术的目的在于针对现有技术不足，提供一种5005H34铝合金板材及其生产方法。该生产方法能保证产品的性能，且能缩短生产流程，通过热轧后，一道次冷轧结合铝卷清洗时采用低温130±10℃烘...
【技术保护点】
一种5005H34铝合金板材，其特征在于：所述铝合金板材的化学成分为：按质量分数计，Si≤0.2%，Fe≤0.55%，Cu≤0.15%，Mn≤0.2%，Mg 0.75~1.0%，Cr≤0.1%，Zn≤0.2%，Ti 0.01~0.05%，其他杂质单个≤0.05%，所有杂质合计≤0.15%，余量为Al。
【技术特征摘要】
1.一种5005H34铝合金板材，其特征在于：所述铝合金板材的化学成分为：按质量分数计，Si≤0.2%，Fe≤0.55%，Cu≤0.15%，Mn≤0.2%，Mg0.75~1.0%，Cr≤0.1%，Zn≤0.2%，Ti0.01~0.05%，其他杂质单个≤0.05%，所有杂质合计≤0.15%，余量为Al。2.一种如权利要求1所述的5005H34铝合金板材的生产方法，其特征在于：以铝锭为原料，经熔铸后得到铸锭，将所得铸锭再经锯切、铣面、铸锭加热、热轧、冷轧、清洗烘烤和精整裁剪，制得厚度为2.0~3.0mm且状态为5005H34铝合金板材。3.根据权利要求2所述的5005H34铝合金板材的生产方法，所述熔铸的工艺参数为：熔炼温度730~750℃，精炼温度725~735℃，铸造温度685~695℃。4.根据权利要求2所述的5005H34...
【专利技术属性】
技术研发人员：吴建新，乔建博，徐始祥，刘华春，郑智滨，
申请(专利权)人：中铝瑞闽股份有限公司，
类型：发明
国别省市：福建,35