The present invention provides a method for preparing nano W Re alloy powder, which belongs to the technical field of powder metallurgy powder preparation. The preparation method is: using ammonium metatungstate, ammonium rhenium, fuel and ammonium nitrate as the raw material, the low temperature synthesis of oxide powder combustion, then use hydrogen reduction to prepare W nano Re alloy powder. The low temperature combustion synthesis method adopted by the invention belongs to the liquid phase synthesis method, which can achieve the mixing of molecular grade. The tungsten oxide and rhenium oxide in the precursor are uniformly mixed, and the reduction product is alloy powder without any subsequent special treatment. In addition, the raw material of the method is simple and easy to get, the equipment is simple, the process is fast, and it is suitable for large-scale production.
【技术实现步骤摘要】
一种制备纳米W-Re合金粉末的方法
本专利技术属于粉末冶金领域，涉及制备纳米W-Re合金粉末的方法。
技术介绍
钨(W)具有高熔点、高硬度，良好的高温强度、导热、导电性能，在国防军工、核工业及高温领域有很广泛的应用。但是W合金在高温下会发生再结晶，严重恶化其力学性能，影响其使用寿命。在W合金中加入Re元素可以显著地提高W合金的再结晶温度，从而改善W合金的高温力学性能，提高其最高使用温度。W-Re合金的传统制备方法是先将W粉与Re粉使用球磨的方法混合，然后通过压制和垂熔烧结工艺制得钨合金，再经过后续变形处理来制备不同类型的W-Re合金材料。专利CN102130288A使用固固混合的方法制备预合金粉末，将W粉与铼酸铵通过球磨混合，混合粉末经过煅烧后用酒精分散，分散后的粉末经过还原、成形、垂熔烧结、旋锻和拉拔工艺制得W-Re合金丝材。专利CN102816963A使用固液混合(钨粉与铼酸铵溶液)的方法制备W-Re合金粉末，再将粉末还原后进行压制和垂熔烧结制备出W-Re合金。这些方法制备的W-Re合金粉末的均匀性较差，且粉末粒度较大，烧结活性差，需要很高的烧结温度或很长的烧...
【技术保护点】
一种制备纳米W‑Re合金粉末的方法，其特征在于制备步骤如下1)采用低温燃烧合成法制备前驱体，具体过程是：将偏钨酸铵、铼酸铵、燃料、硝酸铵按一定的摩尔比例溶解于去离子水中配置成水溶液，将溶液加热至发生燃烧反应，得到蓬松的前驱体粉末；2)将得到的前驱体粉末研磨，然后使用氢气还原即得到纳米W‑Re合金粉末。
【技术特征摘要】
1.一种制备纳米W-Re合金粉末的方法，其特征在于制备步骤如下1)采用低温燃烧合成法制备前驱体，具体过程是：将偏钨酸铵、铼酸铵、燃料、硝酸铵按一定的摩尔比例溶解于去离子水中配置成水溶液，将溶液加热至发生燃烧反应，得到蓬松的前驱体粉末；2)将得到的前驱体粉末研磨，然后使用氢气还原即得到纳米W-Re合金粉末。2.如权利要求1所述一种制备纳米W-Re合金粉末的方法，其特征在于步骤(1)中的燃料为甘氨酸、尿素、EDT...
【专利技术属性】
技术研发人员：秦明礼，陈铮，陈鹏起，鲁慧峰，吴昊阳，贾宝瑞，曲选辉，