The invention discloses a method for preparing a composite casting aluminum bronze valve plate, consists of the following steps: step one, the coated sand mold cavity into the valve plate, the insulation coated sand curing molding mould to coated sand shell; step two, the inner core sleeve is fixed on the copper coated sand shell on the following type and vertical clamping, form a casting cavity; copper sleeve component for aluminum bronze; step three, the liquid iron, after pouring, pouring into the cavity, was casting; step four, casting, cooling, blasting finishes, the coated sand shell composite casting valve plate. By adopting the preparation process of the invention, the qualified rate of the composite casting can be more than 96%, and the technology of the invention solves the technical problem of mass production in the long run of the existing technology.
【技术实现步骤摘要】
一种铝青铜复合铸造阀板的制备方法
本专利技术属于铸造
，具体涉及一种铝青铜复合铸造阀板的制备方法。
技术介绍
壳型铸造是利用覆膜砂工艺而衍生的一种新型的铸造工艺，具体而言是使用酚醛树脂覆膜砂，而非普通砂型，在180-280度的模板上形成合适厚度的薄壳，通常情况下，薄壳的厚度为6-12mm，之后将薄壳进行加温固化，使薄壳达到所需要的刚度和强度，然后利用薄壳构成造型腔，进而生产各种铸件。壳型铸造工艺效果优异，铸造的铸件轮廓清晰，表面光洁，尺寸精确，后续大大减少了机械加工的工作量。但由于现有方法采用了水平分型浇注，导致复合铸件中的铜套在型腔内固定困难，容易偏位，铸件容易产生气孔缺陷，成品合格率低，只有达到70％左右，难以满足规模化生产的要求。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种铝青铜复合铸造阀板的制备方法，节约铸造企业造型材料的成本，操作简单。本专利技术提供的一种铝青铜复合铸造阀板的制备方法，包括以下步骤：（1）取覆膜砂射入阀板模腔，保温使得覆膜砂固化成型，起模，得覆膜砂壳型；（2）将铜套固定在覆膜砂壳型的内芯上，之后...
【技术保护点】
一种铝青铜复合铸造阀板的制备方法，其特征在于：包括以下步骤：（1）取覆膜砂射入阀板模腔，保温使得覆膜砂固化成型，起模，得覆膜砂壳型；（2）将铜套固定在覆膜砂壳型的内芯上，之后合型并垂直夹紧，形成浇注型腔；铜套的组分为铝青铜，铝青铜的组分具体为：铝6.5‑11.2％,铁0.35‑0.60％，锰1.7‑1.9％，硅0.08‑0.12％，锌0.66‑0.97％，锡0.06‑0.09％，镍0.36‑0.49％，铅0.01‑0.02％，余量为铜；（3）取铁液，之后将铁液浇注到浇注型腔中，得铸件；（4）取铸件，冷却，抛丸精整，即得铝青铜复合铸造阀板的制备方法。
【技术特征摘要】
1.一种铝青铜复合铸造阀板的制备方法，其特征在于：包括以下步骤：（1）取覆膜砂射入阀板模腔，保温使得覆膜砂固化成型，起模，得覆膜砂壳型；（2）将铜套固定在覆膜砂壳型的内芯上，之后合型并垂直夹紧，形成浇注型腔；铜套的组分为铝青铜，铝青铜的组分具体为：铝6.5-11.2％,铁0.3...
【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37