一种铝钛合金杆的生产工艺制造技术

本发明专利技术属于合金生产技术领域，提出了一种铝钛合金杆的生产工艺，包括以下步骤：将铝锭加入熔炉内熔化并升温至720‑780℃；向步骤(1)得到的铝液中加入金属钛和扩散剂，搅拌均匀后，控制温度在1000‑1200℃合金化60‑75min；加入精炼剂进行精炼处理；连铸连轧；收线；复烧；断杆。通过上述技术方案，解决了现有技术中铝钛合金块存在TiAl3分布不均匀及TiAl3沉淀聚集所造成偏析的问题。

Production process of a kind of aluminum titanium alloy rod

The invention belongs to the technical field of alloy production, the production process of an aluminum titanium alloy rod is proposed, which comprises the following steps: adding aluminum melting furnace and heated to 720 DEG C to 780 steps; (1) the aluminum liquid adding titanium and dispersing agent, mixing evenly, control the temperature of 60 75min in 1000 1200 DEG C alloy refining agent is added; refining; continuous casting and rolling; winding; sintering; broken rod. Through the above technical scheme, the problem of segregation of TiAl3 distribution and TiAl3 precipitation aggregation in the aluminum and titanium alloy blocks in the existing technology is solved.

【技术实现步骤摘要】
一种铝钛合金杆的生产工艺
本专利技术属于合金生产
，涉及一种铝钛合金杆的生产工艺。
技术介绍
铝钛合金是一种金属材料，具有压铸成品率高，铸件致密、成品强度高、无断裂的特点、柔韧性强、同时镀铜着色效果佳，比重轻。现有技术中的铝钛合金块存在TiAl3分布不均匀的问题，导致最终铝钛合金块的质量不能满足用户需求。
技术实现思路
本专利技术提出一种铝钛合金杆的生产工艺，解决了现有技术中铝钛合金块存在TiAl3分布不均匀的问题。本专利技术的技术方案是这样实现的：一种铝钛合金杆的生产工艺，包括以下步骤：(1)将铝锭加入熔炉内熔化并升温至720-780℃，(2)向步骤(1)得到的铝液中加入金属钛和扩散剂，强力搅拌均匀后，控制温度在1000-1200℃合金化60-75min，(3)加入精炼剂进行精炼处理，(4)连铸连轧，(5)收线，(6)复烧，(7)断杆。进一步，铝锭和扩散剂的质量比为100：1.5-2。进一步，所述扩散剂由以下重量组分的物质组成：氯化钠10-14、氯化钾8-10、氯化镁9-12、氟化铝15-18、氯化钡10-12、氯化铈23-28、氟铝酸钠15-20和氟化钙5-8。本专利技术的有益本文档来自技高网...

【技术保护点】
一种铝钛合金杆的生产工艺，其特征在于：包括以下步骤：(1)将铝锭加入熔炉内熔化并升温至720‑780℃，(2)向步骤(1)得到的铝液中加入金属钛和扩散剂，搅拌均匀后，控制温度在1000‑1200℃合金化60‑75min，(3)加入精炼剂进行精炼处理，(4)连铸连轧，(5)收线，(6)复烧，(7)断杆。

【技术特征摘要】
1.一种铝钛合金杆的生产工艺，其特征在于：包括以下步骤：(1)将铝锭加入熔炉内熔化并升温至720-780℃，(2)向步骤(1)得到的铝液中加入金属钛和扩散剂，搅拌均匀后，控制温度在1000-1200℃合金化60-75min，(3)加入精炼剂进行精炼处理，(4)连铸连轧，(5)收线，(6)复烧，(7)断杆。2.根据权利要求...

【专利技术属性】
技术研发人员：郭成海，范铁林，王全龙，陈致宝，
申请(专利权)人：河北晶宝新金属有限公司，
类型：发明
国别省市：河北,13