The invention discloses a method for the production of polyester filament masterbatch and its preparation method and application, to solve the traditional regeneration masterbatch can have characteristic properties and low cost close to native masterbatch, the technological scheme includes the following components by weight: waste plastic bottles slice 60~70 parts, 10~40 parts, eliminating native masterbatch global masterbatch 1~3, compatibilizer 1~5, accelerator 0.1~1, prepared by the above formula masterbatch has the advantages of low cost, and has excellent performance close to native masterbatch, but also in the production of polyester filament, better compatibility with waste plastic bottles made of polyester filament sections, texture and color are very uniform.
【技术实现步骤摘要】
用于涤纶长丝生产的母粒及其制备方法和应用
本专利技术涉及母粒，特别涉及一种用于涤纶长丝生产的母粒及其制备方法和应用。
技术介绍
涤纶长丝也称聚酯长丝，是指聚对苯二甲酸乙二醇酯为原料生产合成的纤维。由聚酯切片和色母粒经过高温熔融抽丝而成，具有色牢度高、环保、无需染色等优点，被誉为“纺织工业的一次革命”。在有色涤纶长丝生产中，按照计算机测配色得到有色纺丝的色母粒配方后，按配方称取所需三原色色母粒并充分混合均匀，再将复合色母粒干燥后精确计量连续注入螺杆挤压机，使复配色母粒与PET切片混合，连续进入螺杆挤压区，在螺杆挤压熔融过程中充分混合均匀，然后进行纺丝。目前，现有专利中授权公告号为CN103114346B的中国专利公开了一种有钻石闪光效果的有色涤纶长丝及其制备方法，将涤纶切片干燥后经螺杆挤出机熔融挤出，同时采用色母粒注射器向螺杆挤出机注入色母粒，然后进行纺丝。但是，上述专利和现有技术中或者完全采用原生母粒进行纺丝，则成本太大；或者完全采用再生聚酯切片，则性能达不到所需要求，严重影响涤纶纺丝领域的发展。
技术实现思路
本专利技术的目的是提供一种能够保持较低的生产成本且具有较...
【技术保护点】
一种用于涤纶长丝生产的母粒，其特征在于包括如下重量份的组分：废旧塑料瓶切片 60~70份；原生母粒 10~40份；消泡母粒 1~3份；增容剂 1~5份；促进剂 0.1~1份。
【技术特征摘要】
1.一种用于涤纶长丝生产的母粒，其特征在于包括如下重量份的组分：废旧塑料瓶切片60~70份；原生母粒10~40份；消泡母粒1~3份；增容剂1~5份；促进剂0.1~1份。2.根据权利要求1所述的用于涤纶长丝生产的母粒，其特征在于：所述废旧塑料瓶切片的平均密度为1.45~1.5g/cm3。3.根据权利要求1所述的用于涤纶长丝生产的母粒，其特征在于：所述消泡母粒为二甲基硅油与气相二氧化硅以重量比为3:7复合形成的球状团聚体。4.根据权利要求1所述的用于涤纶长丝生产的母粒，其特征在于：所述促进剂包括滑石粉、硅酸钙或者硬脂酸钙中的一种，并与聚乙二醇二缩水甘油醚掺混形成的混合物，其中滑石粉、硅酸钙或者硬脂酸钙中的一种在促进剂中的重量百分比为50~60%。5.根据权利要求1所述的用于涤纶长丝生产的母粒，其特征在于：所述增容剂选用甲基丙烯酸缩水甘油酯、乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯共聚物、马来酸酐-乙烯-醋酸乙烯共聚物中的一种。6.一种如权利要求1~5任意一项所述的用于涤纶长丝生产的母粒的制备方法，其特征在于包括如下步骤：（1...
【专利技术属性】
技术研发人员：钱菊男，
申请(专利权)人：苏州市苏宏塑料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。