The invention discloses a process for preparing furan resin sand, which comprises the following steps: 1) the first of the original sand according to the weight of a copy of the original One divides into two., sand into the continuous mixer, then add to the furan resin sand mixing, adding silane, mixing sand for resin sand; 2) the curing agent is added to another copy of the original sand, sand after sand sand obtained curing agent; 3) will step resin and curing agent according to the proportion of sand mixing, adding sawdust in the mixing process, after mixing for furan resin sand; sand containing sand and reclaimed sand, new sand containing chromite sand. The invention has the characteristics of high strength, good uniformity, good retreat and low production cost, and can reduce the bad rate of castings after use.
【技术实现步骤摘要】
一种呋喃树脂砂的配制工艺
本专利技术属于铸造
，具体涉及一种呋喃树脂砂的配制工艺。
技术介绍
呋喃树脂砂一般由硅砂、树脂和固化剂混合配制而成，具有尺寸精度高、生产周期短、铸型溃散性好、抗拉强度高等诸多优点，可用于铸钢、铸铁及铸造有色合金铸件的生产。现有技术制造呋喃树脂砂多将原砂和呋喃树脂粘接剂在混砂机内充分搅拌，再加入硼酸即固化剂混制均匀，造型时，将混好的型砂放入砂箱，利用树脂和固化剂反应的化学方法进行固化成型。利用该方法配制的呋喃树脂砂退让性差，混砂不均匀，同时因导热性差以至于铸件在凝固收缩时得不到及时补缩造成薄壁钢铸件形成缩裂纹的不良。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种呋喃树脂砂的配制工艺，混砂均匀，退让性得到很大改善，同时大大降低因为缩裂纹而造成的铸件不良率。本专利技术提供的一种呋喃树脂砂的配制工艺，包括以下步骤：1)先将原砂按照重量一分为二，取一份原砂加入连续式混砂机中，然后加入呋喃树脂进行混砂，混砂5-9min后再加入硅烷，混合均匀后出砂获得树脂砂；2）将固化剂加入到另一份原砂中，混砂4-6min后出...
【技术保护点】
一种呋喃树脂砂的配制工艺，其特征在于：包括以下步骤：1）先将原砂按照重量一分为二，取一份原砂加入连续式混砂机中，然后加入呋喃树脂进行混砂，混砂 5‑9min 后再加入硅烷，混合均匀后出砂获得树脂砂；2）将固化剂加入到另一份原砂中，混砂4‑6min后出砂获得固化剂砂；3）将步骤 1) 所得树脂砂和步骤2）所得固化剂砂按1:3的比例搅拌均匀，在搅拌过程中边搅拌边加入木屑，搅拌 20‑35min后获得呋喃树脂砂；原砂中含有重量比为1:5的新砂和再生砂，新砂中含有占新砂总重量30%的铬铁矿砂，呋喃树脂的加入量为原砂总重量的 1.5‑3.8%，固化剂的加入量为呋喃树脂加入量的 40‑...
【技术特征摘要】
1.一种呋喃树脂砂的配制工艺，其特征在于：包括以下步骤：1）先将原砂按照重量一分为二，取一份原砂加入连续式混砂机中，然后加入呋喃树脂进行混砂，混砂5-9min后再加入硅烷，混合均匀后出砂获得树脂砂；2）将固化剂加入到另一份原砂中，混砂4-6min后出砂获得固化剂砂；3）将步骤1)所得树脂砂和步骤2）所得固化剂砂按1:3的比例搅拌均...