递增式辊压轧制法制造技术

递增式辊压轧制法，涉及一种型材的辊压轧制法的技术领域。在型材折弯处，从15°、30°、45°、60°、75°、80°、85°、90°八次变形过程中，辊印线分散在七个变形点上，七个所述变形点分布在所述外卷边槽钢的折弯内侧。本工艺的轧制产生的内应力都在不同的点上，产品轧制时的内应力得到了释放。工件两边成90度，两小边平整产品的R点上没有深痕和拉伸，板材厚度没有变化同时强度得到了保证，产品表面光洁，客户好评度高。

Incremental rolling rolling method

The incremental rolling rolling process involves the technical field of rolling rolling of a kind of profile. At the bending section, from 15 degrees, 30 degrees, 45 degrees, 60 degrees, 75 degrees, 80 degrees, 85 degrees, 90 degrees to eight times of deformation, the roller print line is scattered on seven deformation points, and the deformation points of seven are distributed inside the bending side of the outer edge channel steel. The internal stress produced by this process is at different points, and the internal stress in the rolling process is released. The two sides of the workpiece are 90 degrees, and the two edges are smooth. There is no deep mark and stretch on the R point of the product. The thickness of the sheet has not changed. Meanwhile, the strength has been guaranteed. The product is clean and the customers have high praise.

【技术实现步骤摘要】
递增式辊压轧制法
本专利技术涉及一种型材的辊压轧制法的

技术介绍
对于一种外卷边槽钢的轧制产品，其生产出来后，经常出现两个小边不平，总是塌边，不成90°，辊印线比较深，而且R部位有拉伸，在与其他型材拼焊时，有缝隙产生虚焊，虚焊点易进水，生锈。直接影响产品的耐用性。针对该产品的质量问题，我们对产品的工艺设计进行了分析和研究，老工艺传统设计是，对每一道边长尺寸是固定不变的，随着角度变形逐步成90°。这种轧制方式在变形轧制时，始终都在一个变形点上，在连续辊压时，变形点上出现拉伸，变薄，使用过程中变形点容易出现断裂。
技术实现思路
为了克服上述缺陷，本专利技术提供一种递增式辊压轧制法。本专利技术在型材折弯处，从15°、30°、45°、60°、75°、80°、85°、90°八次变形过程中，辊印线分散在七个变形点上，七个所述变形点分布在所述外卷边槽钢的折弯内侧。本工艺的轧制产生的内应力都在不同的点上，产品轧制时的内应力得到了释放。工件两边成90度，两小边平整产品的R点上没有深痕和拉伸，板材厚度没有变化同时强度得到了保证，产品表面光洁，客户好评度高。附图说明图1为本专利技术的变形点的结构示意本文档来自技高网...

【技术保护点】
递增式辊压轧制法，其特征在于在型材折弯处，从15°、30°、45°、60°、75°、80°、85°、90°八次变形过程中，辊印线分散在七个变形点上，七个所述变形点分布在所述外卷边槽钢的折弯内侧。

【技术特征摘要】
1.递增式辊压轧制法，其特征在于在型材折弯处，从15°、30°、45°、60°、75°、80°、8...

【专利技术属性】
技术研发人员：丁凤友，房发成，叶君，
申请(专利权)人：扬州瑞铖钢业有限公司，
类型：发明
国别省市：江苏,32