一种改良型焊带冷却液制造技术

本发明专利技术关于一种改良型焊带冷却液，其特征在于：由以下重量份数的原料制成：乙醇20‑40％，丙二醇甲醚10‑20％，对苯二酚6‑15％，水溶性油2‑6％，卡松1‑5％，余量为去离子水。本发明专利技术的焊带用冷却液配方科学合理，冷却性能好，对焊带没有任何腐蚀，在冷却液中加入对苯二酚抗氧化剂可延长焊带长期裸露在空气中不被氧化，使用方便，实用环保，生产简单，原料易得，极大的节省了能源，液体全部恽发后少量水溶性油增加焊带的光洁度，来延长焊带的保质期，不会影响焊接效果。

An improved type of welding belt coolant

The invention relates to an improved welding with cooling liquid, which is characterized in that: made from the following raw materials in parts by weight: 20 40% ethanol, propylene glycol ether 10 20%, 6 15% hydroquinone, water soluble oil 2 6% Kathan, 1 5%, the balance of deionized water. The invention of the welding with cooling liquid for scientific and reasonable formula, good cooling performance, butt welding with no corrosion, adding hydroquinone antioxidants in the coolant can prolong the welding zone exposed is not oxidized in the air, easy to use, practical and environmental protection, simple production, raw materials, greatly saves energy, all liquid Yun after a small amount of water soluble oil to increase welding with the finish welding with to prolong the shelf life, will not affect the welding effect.

【技术实现步骤摘要】
一种改良型焊带冷却液
本专利技术涉及太阳能光伏焊带加工领域，尤其关于一种改良型焊带冷却液。
技术介绍
太阳能行业飞速发展，使得太阳能电池片内的焊带加工技术已经成为该行业产品最终走向消费者的重要环节，焊带的加工效果直接决定了电池片的使用寿命及能量转换效率。焊带的涂锡是焊接前的必要工序，由于现在焊带加工技术压延、涂锡成为一体，而收线速度已达到每分90米向上，涂锡后焊带上面的温度在空气中来不及冷却就被收线轮收起，从而影响焊带的质量。
技术实现思路
：本专利技术提供一种改良型焊带冷却液，其可对加工过程中的焊带快速冷却，冷却液附在焊带上还可快速恽发，对焊带没有任何腐蚀且起到保护的作用。为解决上述技术问题，本专利技术所采取的技术方案是：一种改良型焊带冷却液，其特征在于：由以下重量份数的原料制成：上述的焊带用冷却液由以下重量份数的原料制成：本专利技术的优点是：本专利技术一种改良型焊带冷却液，配方科学合理，冷却性能好，对焊带没有任何腐蚀，在冷却液中加入对苯二酚抗氧化剂可延长焊带长期裸露在空气中不被氧化，使用方便，实用环保，生产简单，原料易得，极大的节省了能源，液体全部恽发后少量水溶性油增加焊带的光洁度，本文档来自技高网...

【技术保护点】
一种改良型焊带冷却液，其特征在于：由以下重量份数的原料制成：

【技术特征摘要】
1.一种改良型焊带冷却液，其特征在于：由以下重量份数的原料制成：2.根据...

【专利技术属性】
技术研发人员：郭宏彬，
申请(专利权)人：江苏太阳科技股份有限公司，
类型：发明
国别省市：江苏,32