The invention discloses a method for preparing high performance adhesives for plywood, prepared in accordance with the following steps: the reaction vessel required for cleaning; thiourea and Magnesium Oxide into a container, then add the right amount of tea water, heated to 50 DEG C 60, for heating and stirring; adding stearic acid and the modified epoxy resin, polyether amine and Zinc Oxide to another container, add in the rest of the tea water is heated to 50 DEG C, 60, heating and stirring; the steps 2 and 3 of the mixture, adding curing agent, heating to 30 40 DEG C, stirring 20 30min; natural cooling to room temperature, you can. The beneficial effect of the invention is as follows: good bonding effect, simple production process, low cost, no formaldehyde, little harm to human body and no pollution to the environment.
【技术实现步骤摘要】
一种高性能胶合板粘合剂的制备方法
本专利技术涉及一种木材粘合剂，特别涉及一种高性能胶合板粘合剂的制备方法。
技术介绍
目前的粘合剂种类很多，但木材粘合剂还比较少，而且存在一定不足，粘合强度低、耐水性差、生产工艺复杂、成本高，且含有甲醛，污染环境。
技术实现思路
本专利技术的目的在于克服现有技术中所存在的上述不足，提供一种高性能胶合板粘合剂的制备方法。为了实现上述专利技术目的，本专利技术提供了以下技术方案：一种高性能胶合板粘合剂的制备方法，按照以下步骤进行制备：（1）现将所需的反应容器进行清洗；（2）向容器里加入硫脲和氧化镁，再加入适量的茶叶水，加热至50-60℃，加热的同时进行搅拌；（3）向另一容器里加入硬脂酸、改性环氧树脂、聚醚胺和氧化锌，加入剩下的茶叶水，加热至50-60℃，加热的同时进行搅拌；（4）将步骤2和步骤3得到的混合物混合，加入固化剂，加热至30-40℃，搅拌20-30min；（5）自然冷却到室温，即可。与现有技术相比，本专利技术的有益效果：有粘接效果好、生产工艺简单、成本低廉，且不含有甲醛，对人体的伤害小，不污染环境。具体实施方式下面结合试验例及具体实...
【技术保护点】
一种高性能胶合板粘合剂的制备方法，其特征在于，按照以下步骤进行制备：（1）现将所需的反应容器进行清洗；（2）向容器里加入硫脲和氧化镁，再加入适量的茶叶水，加热至50‑60℃，加热的同时进行搅拌；（3）向另一容器里加入硬脂酸、改性环氧树脂、聚醚胺和氧化锌，加入剩下的茶叶水，加热至50‑60℃，加热的同时进行搅拌；（4）将步骤2和步骤3得到的混合物混合，加入固化剂，加热至30‑40℃，搅拌20‑30min；（5）自然冷却到室温，即可。
【技术特征摘要】
1.一种高性能胶合板粘合剂的制备方法，其特征在于，按照以下步骤进行制备：（1）现将所需的反应容器进行清洗；（2）向容器里加入硫脲和氧化镁，再加入适量的茶叶水，加热至50-60℃，加热的同时进行搅拌；（3）向另一容器里加...
【专利技术属性】
技术研发人员：黄开满，
申请(专利权)人：四川美登家具有限公司，
类型：发明
国别省市：四川,51