The invention provides a halogen-free flame retardant three EPDM, its raw materials by weight: three 50~120 phr, 20~30 phenolic resin, two of benzene quinone 4~8 copies, 2~5 copies of 1 kaolin, sulfur 2.5, polyethylene glycol 3~6, ammonium polyphosphate 4.5 ~ 7, 5~10 aluminum hydroxide a. In the three way ethylene propylene rubber, aluminum hydroxide and ammonium polyphosphate are used as halogen free flame retardants to avoid the harm of traditional halogenated flame retardants when they burn. The addition of aluminum hydroxide and ammonium polyphosphate played a good flame retardant effect and improved the flame retardancy and wear resistance of three ethylene propylene rubber.
【技术实现步骤摘要】
一种无卤阻燃三元乙丙橡胶
本专利技术涉及橡胶
，具体涉及一种无卤阻燃三元乙丙橡胶。
技术介绍
三元乙丙橡胶是乙烯、丙烯和非共轭二烯的共聚物，三元乙丙橡胶分子主链为饱和结构，仅分子侧链有少量不饱和基团，独特的分子结构使三元乙丙橡胶具有优异的耐老化、耐臭氧、耐腐蚀、电绝缘等性能，被广泛应用于建筑、汽车配件、电缆电线等领域。但三元乙丙橡胶属于碳氢材料，氧指数仅为19左右，非常容易燃烧，且燃烧时生烟量较大，这些都极大限制了其应用。为了解决其易燃的问题，需在三元乙丙橡胶中添加阻燃剂。传统的阻燃方法是在三元乙丙橡胶中添加阻燃效率较高的卤/锑阻燃体系，这类阻燃剂添加量小，对材料的力学性能和加工性能影响较小，但在燃烧时会产生大量的烟雾以及有毒、有腐蚀性的卤化氢气体，造成二次污染，很多国家颁布了关于限制使用卤素阻燃剂的法规。目前，国内外对三元乙丙橡胶阻燃的研究方向由传统的卤素阻燃剂向无毒、无卤、绿色环保的阻燃剂转变。
技术实现思路
针对现有技术存在的技术问题，本专利技术提出了一种无卤阻燃三元乙丙橡胶，该橡胶具有优异的弹性和阻燃性能，同时耐老化性和耐磨抗撕裂性能良好。本专利技术是通...
【技术保护点】
一种无卤阻燃三元乙丙橡胶，其特征在于，其原料按重量份包括：三元乙丙橡胶50～120份，酚醛树脂20～30份，对苯二醌4～8份，高岭土2～5份，硫磺1～2.5份，聚乙二醇3～6份，聚磷酸铵4.5～7份，氢氧化铝5～10份。先将氢化三元乙丙橡胶、酚醛树脂和聚乙二醇在密炼机上进行塑炼5～8min，转速60～75r/min，然后混炼3～5min，转速50‑55r/min；按比例加入高岭土和对苯二醌混炼8～10min，再加入环保阻燃剂聚磷酸铵和氢氧化铝混炼10～15min，温度为120‑130℃时排胶；加入不溶性硫磺，在硫化机中进行硫化；对硫化后的三元乙丙橡胶热压成型即得到所述无卤阻燃三元乙丙橡胶。
【技术特征摘要】
1.一种无卤阻燃三元乙丙橡胶，其特征在于，其原料按重量份包括：三元乙丙橡胶50～120份，酚醛树脂20～30份，对苯二醌4～8份，高岭土2～5份，硫磺1～2.5份，聚乙二醇3～6份，聚磷酸铵4.5～7份，氢氧化铝5～10份。先将氢化三元乙丙橡胶、酚醛树脂和聚乙二醇在密炼机上进行塑炼5～8min，转速60～75r/min，然后混炼3～5min，转速50-55r/min；按比例加入高岭土和对苯二醌混炼8～10min，再加入环保阻燃剂聚磷酸铵和氢氧化铝混炼10～15min，温度为120-130℃时排胶；加入不溶性硫磺，在硫化机中进行硫化；对硫化后的三元乙丙橡胶热压成型即得...
【专利技术属性】
技术研发人员：黄志强，
申请(专利权)人：桂林市和鑫防水装饰材料有限公司，
类型：发明
国别省市：广西,45