The invention provides an anti aging three EPDM rubber and a preparation method thereof, prepared from the following components by weight: three Yuan Yibing rubber 160~200, insoluble sulfur 8~15, calcium carbonate 20~30, methyl methacrylate 5~8, two azo formamide 6~9, gallium oxide from 0.8 to 3.5 copies. Two phthalic dicarboximide 1~3 copies, 4~8 copies of ciclopiroxolamine. The preparation methods include mixing, static setting, return refining, vulcanization, anti ultraviolet treatment and hot pressing. The three component ethylene propylene rubber obtained by the invention has excellent aging resistance, tear resistance and abrasion resistance, and has strong ultraviolet resistance, and further prevents aging. The three yuan ethylene propylene rubber is more suitable for harsh environments such as high temperature and exposure to sunlight.
【技术实现步骤摘要】
一种防老化三元乙丙橡胶及其制备方法
本专利技术涉及橡胶
，具体涉及一种防老化三元乙丙橡胶及其制备方法。
技术介绍
三元乙丙橡胶是以乙烯(CH2＝CH2)、丙烯(CH2＝CH-CH3)为主要单体，经溶液聚合并加入不饱和的第三单体(非共轭二烯烃)制成的三元共聚物，属于饱和碳链橡胶。由于三元乙丙橡胶分子链中没有极性取代基团，空间位阻小，分子链比较柔顺，使得三元乙丙橡胶不仅表现出优良的耐屈挠性、回弹性和耐低温性，同时还具有很好的化学结构稳定性，广泛应用于汽车工业、电线电缆、密封材料和耐热制品等领域。虽然三元乙丙橡胶具有优良的化学结构稳定性，但其在实际使用过程中受光、氧、热和化学介质等外界因素的作用，仍会发生一定程度的老化。橡胶的老化除受其本身的分子结构影响外，主要受其工作环境即外部因素的影响，这些外部因素可分为物理因素、化学因素和生物因素三种类型，而每一种类型又包含着很多不同的因素。橡胶的老化易使其性能劣化、制品使用寿命缩短，从而逐渐失去其使用价值。
技术实现思路
本专利技术提供一种防老化三元乙丙橡胶及其制备方法，该防老化三元乙丙橡胶具有较好的耐老化性能，尤其适用于户外...
【技术保护点】
一种防老化三元乙丙橡胶，其特征在于由下述重量份的组分制成：三元乙丙橡胶160～200份，不溶性硫磺8～15份，轻质碳酸钙20～30份，甲基丙烯酸甲酯5～8份，偶氮二甲酰胺6～9份，氧化镓0.8～3.5份，邻苯二甲酰亚胺1～3份，环吡酮胺4～8份。
【技术特征摘要】
1.一种防老化三元乙丙橡胶，其特征在于由下述重量份的组分制成：三元乙丙橡胶160～200份，不溶性硫磺8～15份，轻质碳酸钙20～30份，甲基丙烯酸甲酯5～8份，偶氮二甲酰胺6～9份，氧化镓0.8～3.5份，邻苯二甲酰亚胺1～3份，环吡酮胺4～8份。2.如权利要求1所述的防老化三元乙丙橡胶的制备方法，其特征在于，包括以下步骤：1)按照配比依次将轻质碳酸钙、甲基丙烯酸甲酯和偶氮二甲酰胺加入到三元乙丙橡胶中充分混炼；2)将步骤1)的混炼产物放置10～15h后在混炼机上进行返炼，并加入邻苯二甲酰亚胺和环吡酮胺，再加入不溶性硫磺，在硫化机中进行硫化；3)将氧化镓分散于甲...