The invention provides a method for the synthesis of hydrophobic oil repellent polyurethane modified fluorinated polyacrylate. The steps are as follows: 1) isophorone diisocyanate in the reaction container, adding nitrogen as protective atmosphere of the reaction system, the mixing is heated to 70 DEG C, adding polypropylene glycol, reaction of 3 5h, obtained polyurethane prepolymer; 2) the initiator two azo isobutyronitrile dissolved into the solvent, and adding monomer perfluoroalkyl hexyl ethyl acrylate, hydroxypropyl acrylate and step 1) to obtain a polyurethane prepolymer, stirring at 80 DEG C, the reaction of carbon carbon double bond group system completely after adding an excess of NCO butanone oxime closed vacuum distillation to remove solvent, the product is modified by polyurethane fluorinated polyacrylate.
【技术实现步骤摘要】
一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法
本专利技术属于改性聚氨酯
，具体涉及一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法。
技术介绍
氟烷基丙烯酸酯类聚合物是目前市场上使用的氟烷基织物整理剂的主要成分，这些氟烷基丙烯酸酯类单体价格昂贵，所以产品的生产成本较高。目前全氟烷基丙烯酸酯中的氟烷基基本为长碳链的全氟烷基，这些全氟烷基可明显降低织物表面能，赋予织物优异的拒水拒油性能，但长碳链全氟烷基的市场价格较高，生物降解困难，且具有一定的环境危害性和生物毒性，因此国际上对其在产品中的应用已做出限制。由于氟单体价格昂贵，织物整理剂的生产厂家希望在减少氟烷基单体的用量的同时，不影响其他性能的发挥，从而实现效益最大化。
技术实现思路
为了解决上述技术问题，本专利技术提供了一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法。本专利技术为了实现上述专利技术目的，采用如下的技术方案：一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法，步骤如下：1）将异佛尔酮二异氰酸酯置于反应容器中，通入氮气作为反应体系的保护气氛，搅拌升温至70℃，滴加聚丙二醇，反应3-5h，得到聚氨酯预聚体；2...
【技术保护点】
一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法，其特征在于：步骤如下：将异佛尔酮二异氰酸酯置于反应容器中，通入氮气作为反应体系的保护气氛，搅拌升温至70℃，滴加聚丙二醇，反应3‑5h，得到聚氨酯预聚体；将引发剂偶氮二异丁腈溶解到溶剂中，并加入聚合单体全氟己基乙基丙烯酸酯、丙烯酸羟丙酯和步骤1）得到的聚氨酯预聚体，在80℃下搅拌反应，待体系中碳碳双键基团反应完全后，加入丁酮肟将过量的‑NCO封闭，减压蒸馏除溶剂，所得产物即为聚氨酯改性氟代聚丙烯酸酯。
【技术特征摘要】
1.一种疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法，其特征在于：步骤如下：将异佛尔酮二异氰酸酯置于反应容器中，通入氮气作为反应体系的保护气氛，搅拌升温至70℃，滴加聚丙二醇，反应3-5h，得到聚氨酯预聚体；将引发剂偶氮二异丁腈溶解到溶剂中，并加入聚合单体全氟己基乙基丙烯酸酯、丙烯酸羟丙酯和步骤1）得到的聚氨酯预聚体，在80℃下搅拌反应，待体系中碳碳双键基团反应完全后，加入丁酮肟将过量的-NCO封闭，减压蒸馏除溶剂，所得产物即为聚氨酯改性氟代聚丙烯酸酯。2.根据权利要求1所述的疏水疏油聚氨酯改性氟代聚丙烯酸酯的合成方法，其特征在于：所述的溶剂为甲基...
【专利技术属性】
技术研发人员：王以元，咸曦晨，李洪霞，
申请(专利权)人：摩田化学昆山有限公司，
类型：发明
国别省市：江苏,32