一种应用于运动用品的钛合金及其制造方法技术

本发明专利技术公开一种应用于运动用品的钛合金及其制造方法，其钛合金包含:钛含量为该钛合金之75至96%；铝含量为1至10%；铁含量为0.1至2%；钒含量为0，5至3%、钼合量为0.1至10%、铬含量为0.1至8%、矽合量为0.1%以下、镍含量为0.1%以下及钴含量为0.1%以下，经适当热处理后，其抗拉强度可1200至1300MPa，延伸强度可达8至10%，可应用于高尔夫球本焊头、自行车等运动用品。

A titanium alloy applied to sporting goods and its manufacturing method

The invention discloses a titanium alloy used in sports equipment and its manufacturing method, the titanium alloy contains: the content of titanium and the titanium alloy of 75 to 96%; the content of aluminum is 1 to 10%; the content of iron was 0.1 to 2%; vanadium content of 0, 5 to 3%, 0.1 to 10% the amount of molybdenum, chromium the content of 0.1 to 8%, the silicon content is below 0.1%, nickel content is below 0.1% and the cobalt content is below 0.1%, after proper heat treatment, the tensile strength is 1200 to 1300MPa, the extension strength can reach 8 to 10%, can be applied to the golf head, bicycle sports.

【技术实现步骤摘要】
一种应用于运动用品的钛合金及其制造方法
本专利技术涉及合金及其制造
，特别涉及一种应用于运动用品之高强度、具良好热加工成型性之钛合金及其制作方法。
技术介绍
目前合金技术所开发的钛合金材料，尤其是应用于高夫球焊头、自行车领域之运动用品上之钛合全材料，除应具有高的强度外，还必须兼顾良好的延伸性。美国专利US2006/00.45789中揭示习知Ti-6A1-4V钛合金成分包含5.5至6.75重量百分比之A1，3.5至4.5重量百分比之钒、最大值为0.3重量百分比之铁，以及最大值为0.2重量百分比之氧。-Ti-6A1-4V等习知钛合金材料中，尤以被称为β型钛合金之β相单体所形成的钛合金，大多具有较之以a相为主体的钛合金更具优异的冷车L加工性，而且有许多β型:钛合金可藉由时效处理而获得优异的强度。然而，至日前为止，仍未有优异的热加工成型性超越Ti-6AL-4V，且成本较低，经适当热处理后之性能强度可与SP700合金匹敌，且成本低廉的钛合金材料。
技术实现思路
有鉴于上述缺失本专利技术提供一种机械性能强度高、热加工性极佳的钛合金。本专利技术更包括其钛合金的制造方法。本专利技术所提出之技术手段本文档来自技高网...

【技术保护点】
一种应用于运动用品的钛合金，以其重量百分比计算，包含:钛，其合量为该钛合金之75至96%；铝，其含量为该钛合金之1至10%；铁，其含量为该钛合金之 0.1至2% ；钒，其合量为该钛合金之 0.5至3%；钼，其含量为该钛合金之 0.1至10%；铬，其含量为该钛合金之 0.1至8%；以及一或多种元素选自矽、镍及钴所组成群组，其中该一或多种元素之个别含量为该钛合金之最大值0.1%。

【技术特征摘要】
1.一种应用于运动用品的钛合金，以其重量百分比计算，包含:钛，其合量为该钛合金之75至96%；铝，其含量为该钛合金之1至10%；铁，其含量为该钛合金之0.1至2%；钒，其合量为该钛合金之0.5至3%；钼，其含量为该钛合金之0.1至10%；铬，其含量为该钛合金之0.1至8%；以及一或多种元素选自矽、镍及钴所组成群组，其中该一或多种元素之个别含量为该钛合金之最大值0.1%。2.根据权利要求1所述的一种应用于运...

【专利技术属性】
技术研发人员：戴明坚，
申请(专利权)人：五华县新锐科技有限公司，
类型：发明
国别省市：广东,44