The invention relates to a construction method for preparing adhesive, which is characterized in that the steps are as follows: according to the quality of a number, 28~52, polyvinyl alcohol resin acrylic resin 38~66 were mixed, mixed temperature is 60 degrees, the mixing time is 60min, after adding twelve mixed alkyl benzene sulfonic acid sodium 8~22, stearic acid 2~11 a, polyacrylamide 3~17 mix, mixing time of 35min, mixed after heated to 80 degrees, then adding epoxy acrylate 5~12, 8~17 borax, organic bentonite 4~11, sodium silicate powder 1~7, water 24~41 stirring, stirring time 2H, stirring after natural cooling to room temperature to obtain the finished product. The adhesive has good bonding effect and green environmental protection.
【技术实现步骤摘要】
一种建筑用胶粘剂的制备方法
本专利技术涉及一种建筑用胶粘剂的制备方法。
技术介绍
目前，建筑、装潢等行业对建筑胶粘剂的需求日益增加，传统胶粘剂的胶粘强度、防水等指标已经不能满足目前质量要求，并且含有大量的有机添加剂和有机溶剂等有害物质，对于人们的生活居住环境和身体健康产生不良的影响。目前的建筑胶粘剂为了提高胶粘剂的粘结强度会添加多种改性添加剂，对基础树脂进行改性，虽然粘结性能好，但是添加剂的用量越多，成品胶粘剂中的有害物质就越多，对人们的生活居住环境和身体健康的影响就越大，因此，目前社会需要迫切要求高质量、高性能且环保的建筑胶粘剂来替代传统建筑胶粘剂产品。
技术实现思路
本专利技术针对上述问题提出了一种建筑用胶粘剂的制备方法。具体的技术方案如下：一种建筑用胶粘剂的制备方法，其特征在于，按质量份数计，将聚乙烯醇树脂28~52份、丙烯酸树脂38~66份进行混合，混合温度为60度，混合时间为60min，混合结束后加入十二烷基苯磺酸钠8~22份、硬脂酸2~11份、聚丙烯酰胺3~17份混合，混合时间为35min，混合完成后加热至80度，再加入环氧丙烯酸双酯5~12份、硼砂8~17份、有机膨润土4~11份、硅酸钠粉末1~7份、水24~41份继续搅拌，搅拌时间为2H，搅拌完成后自然冷却至常温得到成品。上述一种建筑用胶粘剂的制备方法，其特征在于，有机膨润土的粒径为60-230微米。上述一种建筑用胶粘剂的制备方法，其特征在于，硅酸钠粉末的粒径为50-100微米。上述一种建筑用胶粘剂的制备方法，其特征在于，水为去离子水。本专利技术所得的胶粘剂粘接效果好的同时,绿色环保。具体实施方...
【技术保护点】
一种建筑用胶粘剂的制备方法，其特征在于，步骤如下：按质量份数计，将聚乙烯醇树脂28~52份、丙烯酸树脂38~66份进行混合，混合温度为60度，混合时间为60min，混合结束后加入十二烷基苯磺酸钠8~22份、硬脂酸2~11份、聚丙烯酰胺3~17份混合，混合时间为35min，混合完成后加热至80度，再加入环氧丙烯酸双酯5~12份、硼砂8~17份、有机膨润土4~11份、硅酸钠粉末1~7份、水24~41份继续搅拌，搅拌时间为2H，搅拌完成后自然冷却至常温得到成品。
【技术特征摘要】
1.一种建筑用胶粘剂的制备方法，其特征在于，步骤如下：按质量份数计，将聚乙烯醇树脂28~52份、丙烯酸树脂38~66份进行混合，混合温度为60度，混合时间为60min，混合结束后加入十二烷基苯磺酸钠8~22份、硬脂酸2~11份、聚丙烯酰胺3~17份混合，混合时间为35min，混合完成后加热至80度，再加入环氧丙烯酸双酯5~12份、硼砂8~17份、有机膨润土4~11份...
【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：镇江市太浪新材料科技有限公司，
类型：发明
国别省市：江苏,32