The invention discloses a method for processing industrial waste free drying adhesive, which comprises the following components in parts by weight: cement curing agent 3~8, polyvinyl alcohol 8~15, polyacrylamide 8~12, sodium carbonate 30~48, cement reinforcing agent 30~40, hydroxypropyl methyl cellulose 3~7. The invention is a good bonding properties and low cost, the molding process used in industrial solid waste, can speed up the drying process of molding products, without drying or drying, which can meet the required strength into the furnace, after molding can be stacked directly, saving the occupied space, reduce construction and production cost. Reduce energy consumption.
【技术实现步骤摘要】
处理工业固废用免烘干粘结剂
本专利技术涉及工业固态废弃物再利用
,特别是一种用于工业固废成型再利用使用的粘结剂。
技术介绍
在钢厂生产过程中会产生大量的除尘灰、钢渣等工业固废,在处理工业固废时,通常需要将粉状固废成型后再次入炉,以形成循环经济,减轻环保压力,降低企业生产损耗。目前,在对粉状固废成型后,由于固废量较大,成型后均需要达到一定强度才能入炉,在对成型产品处理的过程中通常有两种方法,一种是烘干法,即投建烘干设备对成型产品进行烘干处理,但是烘干设备普遍投入较大,运行成本很高,而烘干设备自身还需要燃烧消耗,不符合低碳节能环保的要求;第二种方法便是自然晾晒法,即通过在晾晒场地摊平晾晒来达到硬度要求,虽然可以节省固废再利用成本,但存在工作效率低下的缺陷,而且还需要很大的硬化场地,人力成本较高,且刮风时不可避免地会出现粉末扬尘污染环境。
技术实现思路
本专利技术需要解决的技术问题是提供一种应用于工业固废成型再利用过程中使用的免烘干粘结剂,降低建设及生产成本,减少能源消耗。为解决上述技术问题,本专利技术所采取的技术方案如下。处理工业固废用免烘干粘结剂,包括以下重量份数的组分:水泥固化剂3~8份,聚乙烯醇8~15份,聚丙烯酰胺8~12份,碳酸钠30~48份,水泥增强剂30~40份,羟丙基甲基纤维素3~7份。上述处理工业固废用免烘干粘结剂的优选方案为,包括以下重量份数的组分:水泥固化剂3-5份,聚乙烯醇10~15份,聚丙烯酰胺10~12份,碳酸钠40~48份,水泥增强剂35~40份,羟丙基甲基纤维素3~5份。上述处理工业固废用免烘干粘结剂的优选方案为,包括以下重量 ...
【技术保护点】
处理工业固废用免烘干粘结剂,其特征在于,包括以下重量份数的组分:水泥固化剂3~8份,聚乙烯醇8~15份,聚丙烯酰胺8~12份,碳酸钠30~48份,水泥增强剂30~40份,羟丙基甲基纤维素3~7份。
【技术特征摘要】
1.处理工业固废用免烘干粘结剂,其特征在于,包括以下重量份数的组分:水泥固化剂3~8份,聚乙烯醇8~15份,聚丙烯酰胺8~12份,碳酸钠30~48份,水泥增强剂30~40份,羟丙基甲基纤维素3~7份。2.根据权利要求1所述的处理工业固废用免烘干粘结剂,其特征在于,包括以下重量份数的组分:水泥固化剂3-5份,...
【专利技术属性】
技术研发人员:张大亮,
申请(专利权)人:保定市胜辉聚合物科技有限公司,
类型:发明
国别省市:河北,13