The invention discloses a mixed sand concrete, belongs to the field of concrete, concrete is used to reduce the dependence on sand, which comprises the following components: the weight of the fine sand fineness modulus 1.0~1.5; fineness modulus 3.0~4.0 slag; fineness modulus of 4.5~5.5 sand; cement; modified polycarboxylate superplasticizer; water; fly ash; the components according to weight ratio for the mixed ratio of 9:10:15:12:2:10:8. In view of the above technical scheme, the invention can through the ratio of different particle size of sand, thus making full use of river sand, gravel replacement can be further reduced, ensuring the concrete performance, reduce the amount of sand, improve environmental performance.
【技术实现步骤摘要】
混合砂混凝土
本专利技术属于混凝土领域，具体地说，尤其涉及一种混合砂混凝土。
技术介绍
混凝土作为现代城市建筑的主要建筑材料之一，其随着城市规模的不断增加而需求量突飞猛进。现有的混凝土采用的用砂量也随之逐年增加，而这些砂石的来源多为河道砂石。现在人们对于环保的要求越来越高，河道采砂作业对于河道生态的破坏程度也逐渐增加，如何实现混凝土用砂的保障，且不破坏河道的生态环境，成为混凝土生产领域需要解决的问题。
技术实现思路
本专利技术提供了一种混合砂混凝土，其能够采用多种砂石成分的有效配合，避免单一用砂造成的河道破坏，降低混凝土对河砂的依赖，也能够保证混凝土的强度和性能。本专利技术是通过以下技术方案实现的：本专利技术中所述的混合砂混凝土，包括以下重量份的成分组成：细度模数在1.0~1.5的细砂；细度模数在3.0~4.0的矿粉；细度模数在4.5~5.5的中砂；水泥；改性聚羧酸系减水剂；水；粉煤灰；上述各组份按照重量份比例为9：10：15：12：2：10：8的比例混合。进一步地讲，本专利技术中所述的改性聚羧酸系减水剂的减水率为20~23%。与现有技术相比，本专利技术的有益效果是：本专利技术能够通过对不同砂石的粒度进行配比，实现了河道砂石的充分利用，进一步降低砂石的可替换性，在保证混凝土性能的情况下，降低河道砂石的用量，提高环保性能。具体实施方式实施例1：混合砂混凝土，包括以下重量份的成分组成：细度模数在1.0的细砂；细度模数在3.0的矿粉；细度模数在4.5的中砂；水泥；改性聚羧酸系减水剂；水；粉煤灰；上述各组份按照重量份比例为9：10：15：12：2：10：8的比例混合。...
【技术保护点】
一种混合砂混凝土，其特征在于：包括以下重量份的成分组成：细度模数在1.0~1.5的细砂；细度模数在3.0~4.0的矿粉；细度模数在4.5~5.5的中砂；水泥；改性聚羧酸系减水剂；水；粉煤灰；上述各组份按照重量份比例为9：10：15：12：2：10：8的比例混合。
【技术特征摘要】
1.一种混合砂混凝土，其特征在于：包括以下重量份的成分组成：细度模数在1.0~1.5的细砂；细度模数在3.0~4.0的矿粉；细度模数在4.5~5.5的中砂；水泥；改性聚羧酸系减水剂...