The invention discloses an anti slide color thin layer of pavement material, which comprises the following components: corundum, ceramic aggregate, Xuan Wuyan, bauxite, iron steel, steel slag, quartz sand, composite modified epoxy resin and pigment. The composite modified epoxy resin is made up of basic components and curing components. The basic components are composed of epoxy resin, acrylic acid, two octyl sebacate and Muscovite powder, and the curing group is polyamide. The anti slip color thin pavement material has the advantages of high abrasion resistance and high skid resistance. Besides, the pavement material has the advantages of strong color stability, high stability and high water resistance, and is suitable for color road and pavement construction.
【技术实现步骤摘要】
一种抗滑彩色薄层路面材料
本专利技术属于路面铺装材料
，特别是涉及抗滑彩色薄层路面材料。
技术介绍
目前城市道路及住宅小区的道路路面大都是水泥路面、沥青路面，其颜色单一，容易造成驾驶员视觉疲劳。路面的抗裂性能较差，使用一段时间后会出现多处裂痕。路面的摩擦防滑性能也较差，刹车制动距离较长。彩色路面胶结料主要有三种：第一把普通黑沥青脱色再加所需要颜色的颜料制成彩色胶结料；第二用石油树脂+聚合物+芳香油+颜料等制成彩色胶结料；第三种用树脂+固化剂+染料，制成反应固化型彩色胶结料。然而，在水泥路面和沥青路面上加铺彩色路面会遇到很多技术问题。二者间的粘结很容易被外界环境所破坏，进而彩色路面就会随之发生破坏；在沥青混凝土上加铺彩色路面，首先要对旧沥青路面进行铣刨，如果处理不当原有路面就会发生破坏，并且耗时耗力。更为重要的是彩色沥青路面颜色的耐久性差，在使用较短的时间后褪色严重，无法实现长期调节路面颜色的作用。此外，彩色涂层的施加，会影响路面的抗滑性能，使刹车制动距离较长，影响车辆行驶安全。
技术实现思路
本专利技术的目的是提供一种抗滑彩色薄层路面材料，以解决彩色路面颜色耐久...
【技术保护点】
一种抗滑彩色薄层路面材料，其特征在于，包含以下组分：金钢砂、陶瓷骨料、玄武岩、铝矾土、铁钢砂、钢渣、石英砂、复合改性环氧树脂和颜料。
【技术特征摘要】
1.一种抗滑彩色薄层路面材料，其特征在于，包含以下组分：金钢砂、陶瓷骨料、玄武岩、铝矾土、铁钢砂、钢渣、石英砂、复合改性环氧树脂和颜料。2.根据权利要求1所述的抗滑彩色薄层路面材料，其特征在于，由以下重量份的组分构成：金钢砂1～8重量份、陶瓷骨料40～60重量份、玄武岩20～35重量份、铝矾土16～33重量份、铁钢砂18～26重量份、钢渣5～12重量份、石英砂8～20重量份、复合改性环氧树脂20～38重量份、颜料1～5重量份。3.根据权利要求2所述的抗滑彩色薄层路面材料，其特征在于，所述复合改性环氧树脂由基本组分和固化组分构成：基本组分由环氧树脂、丙烯酸、癸二酸二辛酯和白云母粉构成；固化组为聚酰胺。4.根据权利要求3所述的抗滑彩色薄层路面材料，其特征在于，基本组分由以下重量份的组分构成：环氧树脂100重量份、丙烯酸30～50重量份、癸二酸二...
【专利技术属性】
技术研发人员：罗亚军，金晓娟，
申请(专利权)人：重庆海聚道路材料有限公司，
类型：发明
国别省市：重庆,50