The invention belongs to the technical field of environmental protection decoration, in particular relates to a water environmental protection sand and its preparation process. The invention mainly solves the technical problems of the existing outdoor weathering artificial sand, decoloring. The invention is realized through the following technical scheme: a waterborne sand, by the weight of prepared particles: 1000 copies, 10~50 copies of a binder and adhesion promoter 0.1 - 1, 0.2 - 5, water paint 5~20 copies, 10~50 copies of the two binder. Compared with the existing technology, the invention has the advantages of not easy to decolorization, good weather resistance, and so on.
【技术实现步骤摘要】
一种水性环保彩砂及其制备工艺
本专利技术属于环保彩砂
，特别涉及一种水性环保彩砂及其制备工艺。
技术介绍
随着近几年外墙真石质感涂料的广泛应用，真石质感涂料的主材天然彩砂需求量逐年增加，由于天然彩砂属于不可再生资源，而且天然彩砂的开采加工过程又对生态环境造成相当大的破坏，天然彩砂行业注定不是一个可持续发展的行业，其发展将越来越受到政策的制约。天然彩砂受限所造成的空缺则只能由人工彩砂来填补，当前，人工彩砂的制备工艺主要有三种：烧结彩砂、染色彩砂、树脂固化彩砂，其中烧结彩砂工艺最为成熟，已有数家企业形成规模化生产，但这种工艺能耗较大，对材料要求高，成本居高不下；而染色彩砂，易脱色，不耐晒，因缺陷明显，基本不被使用；树脂固化彩砂，户外耐候性差，一般用于室内。因此，如何获得一种品质优异、价格低廉、用途多样、效果丰富的人工彩砂产品，是业内急需解决的问题。
技术实现思路
本专利技术的目的在于克服现有技术的缺点，提供一种水性环保彩砂及其制备工艺，解决现有人工彩砂存在的易脱色、户外耐候性差的技术问题。本专利技术是通过以下技术方案实现的：一种水性环保彩砂，其由下述重量份的原料配制...
【技术保护点】
一种水性环保彩砂，其特征在于：其由下述重量份的原料配制而成：颗粒物1000份、粘结剂一10～50份、附着力促进剂0.1～1份、颜料0.2～5份、水5～20份、粘结剂二10～50份；所述颗粒物为石英砂、玻璃砂、河沙、海沙、沙漠沙、无机硅酸盐颗粒、塑料颗粒、玻璃珠或各类矿渣中的一种；所述粘结剂一为水性环氧树脂、水性丙烯酸树脂、硅溶胶、水性聚氨酯树脂、有机无机复合乳液或丙烯酸乳液中的一种；所述粘结剂二为水性环氧树脂、水性丙烯酸树脂、硅溶胶、水性聚氨酯树脂、有机无机复合乳液或丙烯酸乳液中的一种；所述附着力促进剂为硅烷偶联剂、钛酸酯偶联剂中的一种；所述颜料为氧化铁系颜料、炭黑、酞菁蓝...
【技术特征摘要】
1.一种水性环保彩砂，其特征在于：其由下述重量份的原料配制而成：颗粒物1000份、粘结剂一10～50份、附着力促进剂0.1～1份、颜料0.2～5份、水5～20份、粘结剂二10～50份；所述颗粒物为石英砂、玻璃砂、河沙、海沙、沙漠沙、无机硅酸盐颗粒、塑料颗粒、玻璃珠或各类矿渣中的一种；所述粘结剂一为水性环氧树脂、水性丙烯酸树脂、硅溶胶、水性聚氨酯树脂、有机无机复合乳液或丙烯酸乳液中的一种；所述粘结剂二为水性环氧树脂、水性丙烯酸树脂、硅溶胶、水性聚氨酯树脂、有机无机复合乳液或丙烯酸乳液中的一种；所述附着力促进剂为硅烷偶联剂、钛酸酯偶联剂中的一种；所述颜料为氧化铁系颜料、炭黑、酞菁蓝、酞菁绿、耐晒黄、永固紫、珠光颜料、水性铜金粉、水性铝银粉、蓄光颜料中的一种或几种复配。2.一种如根据权...