The invention relates to a powder metallurgy formula, including graphite powder, copper powder, stearic acid, Zinc Oxide, iron, manganese sulfide, alumina, easy cutting agent, wax powder and reinforcing agent; characterized by mass measurement: 1 5 graphite powder and copper powder, 5 10, stearic acid 2 8 5, Zinc Oxide 8 copies, 98 copies, 50 iron manganese sulfide 1 5 copies, 10 copies of 5 alumina, cutting agent 0.2 0.5 copies, 1 copies and 0.5 wax powder enhancer 0.2 0.5; blank shape is pressed into standby settings in pressure 60 - 70MPa under; the products are blank pieces into the sintering furnace in sintering into semi-finished products; after oil and steam treatment, cleaning finished; the formula of little pollution to the environment, this method simplify the production process, improve production efficiency.
【技术实现步骤摘要】
一种粉末冶金配方及其冶金成型方法
本专利技术涉及粉末冶金领域，尤其涉及一种粉末冶金配方及其冶金成型方法。
技术介绍
粉末冶金是制取金属粉末并通过成形和烧结等工艺将金属粉末与非金属粉末的混合物制成成品的加工方法。通常所采用的粉末冶金工艺，对环境污染较大，而在机械行业中，大家也越来越倡导简化生产步骤，提高生产效率。
技术实现思路
本专利技术要解决的技术问题是提供一种粉末冶金的配方，本专利技术的另一个目的是提供其冶金方法，本配方对环境污染小，本方法简化生产步骤，提高生产效率。为解决上述技术问题，本专利技术的技术方案为：一种粉末冶金配方，包括石墨粉、铜粉、硬脂酸、氧化锌、铁粉、硫化亚锰、氧化铝、易切削剂、微粉蜡和增强剂；其创新点在于：按质量计量：石墨粉1-5份、铜粉5-10份、硬脂酸2-8份、氧化锌5-8份、铁粉50-98份、硫化亚锰1-5份、氧化铝5-10份、易切削剂0.2-0.5份、微粉蜡0.5-1份和增强剂0.2-0.5份；所述石墨粉、铜粉、氧化锌、铁粉、硫化亚锰和氧化铝的粒度均为400-600微米；所述铁粉包括水雾化铁粉和还原铁粉，所述铁粉中水雾化铁粉占质量比为30%...
【技术保护点】
一种粉末冶金配方，包括石墨粉、铜粉、硬脂酸、氧化锌、铁粉、硫化亚锰、氧化铝、易切削剂、微粉蜡和增强剂；其特征在于：按质量计量：石墨粉1‑5份、铜粉5‑10份、硬脂酸2‑8份、氧化锌5‑8份、铁粉50‑98份、硫化亚锰 1‑5 份、氧化铝 5‑10 份、易切削剂0.2‑0.5份、微粉蜡0.5‑1份和增强剂0.2‑0.5份；所述石墨粉、铜粉、氧化锌、铁粉、硫化亚锰和氧化铝的粒度均为 400‑600 微米；所述铁粉包括水雾化铁粉和还原铁粉，所述铁粉中水雾化铁粉占质量比为30%，还原铁粉占质量比为70%。
【技术特征摘要】
1.一种粉末冶金配方，包括石墨粉、铜粉、硬脂酸、氧化锌、铁粉、硫化亚锰、氧化铝、易切削剂、微粉蜡和增强剂；其特征在于：按质量计量：石墨粉1-5份、铜粉5-10份、硬脂酸2-8份、氧化锌5-8份、铁粉50-98份、硫化亚锰1-5份、氧化铝5-10份、易切削剂0.2-0.5份、微粉蜡0.5-1份和增强剂0.2-0.5份；所述石墨粉、铜粉、氧化锌、铁粉、硫化亚锰和氧化铝的粒度均为400-600微米；所述铁粉包括水雾化铁粉和还原铁粉，所述铁粉中水雾化铁粉占质量比为30%，还原铁粉占质量比为70%。2.权利要求1所述的一种粉末冶金配方的冶金成型方法，其特征在于：包括以...
【专利技术属性】
技术研发人员：纪桂林，
申请(专利权)人：南通冠达粉末冶金有限公司，
类型：发明
国别省市：江苏,32