The invention discloses a AS carrier masterbatch, by weight percentage, which comprises the following components: styrene acrylonitrile copolymer AS19.9 ~ 20.1%, 0.1 ~ 0.3%, additive calcium stearate 0.4 ~ 0.6% and 79.2 ~ 79.4% talcum powder; preparation, first put talcum powder, adding polyolefin elastomer mixed, then add the acrylonitrile and styrene copolymer and calcium stearate, finally adding additives, mixing the mixture is heated to 210 DEG C, heating for 15~20 minutes, and then enter the double screw extruder; mixing after extrusion, cooling and cutting. Through the above way, the invention is suitable for plastic modification. Because of its compact form and higher composite quantity, the dispersion of the plastics is good, wear resistance, scratch resistance, easy feeding and good thermal stability.
【技术实现步骤摘要】
一种AS载体母粒
本专利技术涉及塑料材料领域,特指一种很适合用于塑料改性方面,由于其压实的形态、更高的复合量,使塑料的分散性好,耐磨,耐刮擦,易喂料,热稳定性好的AS载体母粒。
技术介绍
母料系增强塑料内被纤维或其他增强材料分散于其中的树脂组分或基料。复合材料中的连续相,称母料或基料;母料是由载体树脂、填料和各种助剂组成的。母料中助剂的限度或填料的含量比实际塑料制品中的需要量要高数倍至十几倍。在成型加工过程中,必须根据母料中有关组分的含量和实际制品中需要加入的量,调节母料与基体树脂的配比。母料通常可以分为普通填充母料(简称填充母料)和功能性母料,如色母料、防雾滴母料等。填充母料的主要组分是填料,主要用于聚烯烃(聚乙烯和聚丙烯)的加工成型,又称为聚烯烃填充母料;但是现有AS载体母粒不能有效的提高塑料的分散性;并且热稳定性也不好。
技术实现思路
本专利技术主要解决的技术问题是提供一种很适合用于塑料改性方面,由于其压实的形态、更高的复合量,使塑料的分散性好,耐磨,耐刮擦,易喂料,热稳定性好的AS载体母粒。为达到上述目的,本专利技术采用的技术方案是:一种AS载体母粒,以重量百分比计,包括如下组分:苯乙烯-丙烯腈共聚物AS19.9~20.1%、助剂0.1~0.3%、硬脂酸钙0.4~0.6%和滑石粉79.2~79.4%;制备时,先投入滑石粉,再加入聚烯烃弹性体混合,然后再加入丙烯晴和苯乙烯的共聚物和硬脂酸钙,最后加入助剂,将混合物密炼加温至210℃,加热15~20分钟,然后进入双螺杆挤出机混炼;混炼后挤出、冷却和切粒。优选的,所述助剂为抗氧化剂。优选的,所述双螺杆挤出机的 ...
【技术保护点】
一种AS载体母粒,其特征在于:以重量百分比计,包括如下组分:苯乙烯‑丙烯腈共聚物AS19.9~20.1%、助剂0.1~0.3%、硬脂酸钙0.4~0.6%和滑石粉79.2~79.4%;制备时,先投入滑石粉,再加入聚烯烃弹性体混合,然后再加入丙烯晴和苯乙烯的共聚物和硬脂酸钙,最后加入助剂,将混合物密炼加温至210℃,加热15~20分钟,然后进入双螺杆挤出机混炼;混炼后挤出、冷却和切粒。
【技术特征摘要】
1.一种AS载体母粒,其特征在于:以重量百分比计,包括如下组分:苯乙烯-丙烯腈共聚物AS19.9~20.1%、助剂0.1~0.3%、硬脂酸钙0.4~0.6%和滑石粉79.2~79.4%;制备时,先投入滑石粉,再加入聚烯烃弹性体混合,然后再加入丙烯晴和苯乙烯的共聚物和硬脂酸钙,最后...
【专利技术属性】
技术研发人员:王银木,
申请(专利权)人:优矿塑新材料科技苏州有限公司,
类型:发明
国别省市:江苏,32