The invention discloses a bathroom basin slurry, the slurry is calculated according to the weight, including the following components: powder 40~70 parts, resin 20~45, titanium dioxide or paste 0.2 ~ 5, 0.1 ~ 2 inhibitor, curing agent 1 ~ 6, 0.5 ~ 3 accelerator; the slurry through add UV curing coating, accelerate the curing slurry process, improve the production efficiency of the enterprise, so as to improve the profits of the product, to enhance the competitiveness of enterprises; with appropriate proportion and specifications of UV curing coatings in the slurry of the powder material, the slurry curing type after sanitary material has good the environmental protection, abrasion resistance, chemical resistance, hardness etc..
【技术实现步骤摘要】
一种卫浴面盆浆料
本专利技术涉及卫浴设备制造
，特别涉及一种卫浴面盆浆料。
技术介绍
卫浴面盆是家居卫生装修不可划缺的一部分，传统的卫浴面盆是由不锈钢、陶瓷等传统建筑材料制成的，陶瓷材质的面盆占据了很大的市场，然而，不锈钢材质的面盆造型单一，不易与卫浴家具搭配使用，陶瓷材质的面盆易碎，不能承受打击或重物的撞击；人造石因其具有无毒性、无放射性、阻燃、不粘油、不渗污、抗菌防霉、耐磨、耐冲击、易保养、无缝拼接、造型百变的优点，逐渐地出现在卫浴产品中。人造石卫浴面盆是运用石粉和化学涂料配成浆料再固化成型而成的，目前市面上很多的人造石卫浴面盆所使用的浆料的环保性能、固化速度以及浆料固化成型后的产品的力学性能等方面还有待提高。可见，现有技术还有待改进和提高。
技术实现思路
鉴于上述现有技术的不足之处，本专利技术的目的在于提供一种卫浴面盆浆料，旨在解决现有技术中由于浆料成分配比的不足造成环保性不够高、固化速度慢以及固化成型后的产品力学性能不足的问题。为了达到上述目的，本专利技术采取了以下技术方案：一种卫浴面盆浆料,其中，该浆料按重量份计算，包括以下组分：石粉40～70份，树脂...
【技术保护点】
一种卫浴面盆浆料，其特征在于，该浆料按重量份计算，包括以下组分：石粉 40～70份，树脂 20～45份，钛白粉或色浆 0.2～5份，阻聚剂 0.1～2份，固化剂 1.0～6份，促进剂 0.5～3份。
【技术特征摘要】
1.一种卫浴面盆浆料，其特征在于，该浆料按重量份计算，包括以下组分：石粉40～70份，树脂20～45份，钛白粉或色浆0.2～5份，阻聚剂0.1～2份，固化剂1.0～6份，促进剂0.5～3份。2.根据权利要求1所述的卫浴面盆浆料，其特征在于，该浆料按重量份计算，包括以下组分：石粉50～70份，树脂20～38份，钛白粉或色浆0.2～3份，阻聚剂0.1～1.2份，固化剂1.0～4.8份，促进剂0.5～2.4份。3.根据权利要求1所述的卫浴面盆浆料，其特征在于，所述的浆料中包括60～65重量份的石粉。4.根据...
【专利技术属性】
技术研发人员：张俊勇，胡成龙，
申请(专利权)人：佛山市品柏智能科技有限公司，
类型：发明
国别省市：广东,44