The utility model discloses a UV type viscosity reducing tape comprises a parting layer, the bottom surface of UV coating, adhesive layer, and PO layer decrease from the bottom, the reduction of UV adhesive peel strength was in the range of 500 2000g/25mm, the UV reduced the thickness of the adhesive layer is 10 230 m; the utility model by using the PO film as the substrate reducing adhesive tape, broaden the application scope of UV reduction of adhesive tape, and structure according to the characteristics of PO films on UV reduction of adhesive tape was improved, the bottom surface of the coating increases the adhesive layer between the reduction in PO film and UV, making PO film and UV the connection between the anti adhesive layer more firmly, improve the ability of UV fixed, reducing the adhesive tape at the same time, when using PO plastic film as substrate, when the tape is stretched when peeled, produced by pulling the tape after the disappearance of the effect of viscosity.
【技术实现步骤摘要】
一种UV减粘型胶带
本技术涉及一种胶带，尤其涉及一种减粘型胶带。
技术介绍
在滤光片等光学镜片玻璃或者是微小元器件进行加工时，通常需要采用胶带辅助固定，避免在切割工艺中由于元器件移动导致损坏。但是用于固定的胶带，其粘贴强度需要严格控制，如果粘贴力过强，容易在拆除胶带时发生损坏元器件的状况，而如果粘贴力过小，则容易无法完全固定元器件导致损坏。现有技术一般采用减粘型胶带进行处理，固定时胶带保持高粘度，保证元器件固定稳固，切割完成后采用一定的手段降低粘度，在去除胶带。但是现有技术仍未做到十分优秀的易剥离性，损坏元器件的情况仍然时有发生。且现有减粘胶带通常采用PET材料制作，该材料并不适用于滤光片的切割工艺，PET极易在该工艺发生损坏导致无法实现固定的元件的作用。
技术实现思路
针对上述不足，技术的目的在于提供一种减粘型胶带，实现优秀的剥离性，保证精细元器件不被损坏，且固定效果好。本技术为达到上述目的所采用的技术方案是：一种UV减粘型胶带，包括由下至上依次设置有离型膜层、UV减粘胶层、底面涂层以及PO膜层。作为本技术的进一步改进，所述PO膜层上方还设置有PET膜层。作为本技术的进...
【技术保护点】
一种UV减粘型胶带，其特征在于，包括由下至上依次设置有离型膜层、UV减粘胶层、底面涂层、以及PO膜层，所述UV减粘胶层的剥离力范围为500‑2000g/25mm，所述UV减粘胶层的厚度为10‑230μm。
【技术特征摘要】
1.一种UV减粘型胶带，其特征在于，包括由下至上依次设置有离型膜层、UV减粘胶层、底面涂层、以及PO膜层，所述UV减粘胶层的剥离力范围为500-2000g/25mm，所述UV减粘胶层的厚度为10-230μm。2.如权利要求1所述的UV减粘型胶带，其特征在于，所述PO膜层上方还设置有PET膜层。3.如权利要求1或2任一项所述的UV减粘...
【专利技术属性】
技术研发人员：蔡金石，李响，金永光，
申请(专利权)人：东莞市明信高分子科技有限公司，
类型：新型
国别省市：广东,44