The invention relates to a cable material field, in particular to a high temperature flame retardant fillers and its preparation method. Its composition is as follows: 25 asbestos 30 copies, 30 copies, 20 wool soft metal particle 18 20, thermoplastic resin 10 12 copies, 7 copies, 5 graphite particle stabilizer 2 4, anti oxidant 2 4 copies, a method for preparing high temperature flame retardant filling rope, the specific steps are as follows: (1) high temperature; (2) is a general term for asbestos fibers, fibrous silicate minerals, has good fireproof, heat insulation, acid and alkali resistance, thermal insulation, sound insulation, anti-corrosion electrical insulation and high tensile strength, and high temperature resistant rock wool, highly flame retardant properties; adding graphite particles and soft metal particles by high temperature fusion, the invention has certain compressive properties.
【技术实现步骤摘要】
一种阻燃高温填充绳及其制备方法
本专利技术涉及电缆材料领域,具体是一种阻燃高温填充绳及其制备方法。
技术介绍
电缆内部的电缆芯在绞合之后会留下少量空隙,一般使用麻、纤维类作为填充料,但麻、纤维类的耐热性能较差,同时阻燃性能不够优越,因此需要对填充绳进行加工以增强性能。
技术实现思路
为了解决上述问题,本专利技术提出一种阻燃高温填充绳及其制备方法。一种阻燃高温填充绳,其具体组成如下:石棉25-30份、岩棉20-30份、软金属粒18-20份、热塑性树脂10-12份、石墨粒5-7份、稳定剂2-4份、抗氧化剂2-4份。所述的热塑性树脂为含环氧基的苯乙烯共聚物。一种阻燃高温填充绳的制备方法,其具体步骤如下:(1)高温:使用高温将软金属粒与热塑性树脂粘结在一起,同时加入石墨粒、稳定剂和抗氧化剂搅拌均匀;(2)纤维:将石棉和岩棉投入到步骤(1)的混合物中,搅拌后使用挤出机挤出冷却即可。本专利技术的有益效果是:石棉为是纤维状硅酸盐矿物的总称,具有优良的防火、绝热、耐酸、耐碱、保温、隔声、防腐、电绝缘性和较高的抗拉强度,与耐高温的岩棉使用,具有高度阻燃性能;添加石墨粒和软金属粒经过高温融合,使得本专利技术具有一定的抗压性能。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白了解,下面对本专利技术进一步阐述。实施例一:一种阻燃高温填充绳,其具体组成如下:石棉30份、岩棉25份、软金属粒18份、热塑性树脂12份、石墨粒6份、稳定剂2份、抗氧化剂4份。所述的热塑性树脂为含环氧基的苯乙烯共聚物。一种阻燃高温填充绳的制备方法,其具体步骤如下:(1)高温:使用高温 ...
【技术保护点】
一种阻燃高温填充绳,其特征在于:其具体组成如下:石棉25‑30份、岩棉20‑30份、软金属粒18‑20份、热塑性树脂10‑12份、石墨粒5‑7份、稳定剂2‑4份、抗氧化剂2‑4份。
【技术特征摘要】
1.一种阻燃高温填充绳,其特征在于:其具体组成如下:石棉25-30份、岩棉20-30份、软金属粒18-20份、热塑性树脂10-12份、石墨粒5-7份、稳定剂2-4份、抗氧化剂2-4份。2.根据权利要求1所述的一种阻燃高温填充绳,其特征在于:所述的热塑性树脂为含环氧基的苯乙烯共...
【专利技术属性】
技术研发人员:后忠,
申请(专利权)人:芜湖缆胜电缆新材料有限公司,
类型:发明
国别省市:安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。